very nice and a lot of info, way to go. I noticed you must have access to plenty of the needed chemicals, some of which are hard or even impossible to get these days (i.e. HNO3). Hence my question, is it possible to achieve the same result using only the minimal amount of chemicals, for instance, you need a lot of de-NOx-ing product so perhaps it's possible to use less HNO3 to start with? Kind regards
WOW! That was an awesome yield from those hefty pins. Was there any silver recovered during these two processes? Love that deep orange colored liquid on the second refine!
A while back I was experimenting to recover pin gold with sulfuric acid and an electric current, aqua regia, sulfamic acid and sodium metabisulfite and I did not get good results. I would like to test your method, but I want to ask you if you could give me your detailed procedure in writing so that I can understand it correctly and not fail again, I will greatly appreciate it, thank you very much, I have been your subscriber for years, I will continue to watch your videos, thank you ... .
@@OwlTech333 Oh yeah. Its sad but of course you still need a HCL wash for one or two minutes with HCL before you use iodine or any other less harmful solution. Yeah, the remaining solder is realy an issue ...
Cho tôi hỏi lúc ngâm hno3+ 50g citric ngâm mấy h? How time và để vậy + hno3 vào ngâm tiếp hay rữa sạch rồi mới thêm hno3 vào anh? Trong bình bột xanh nó ra nhiều quá làm cách nào a
Sir! It's really awesome Would you like to share full details about this process like purity of chemicals and quantity of chemicals kindly consider thiz comment tq so much sir :)
@@OwlTech333 Can you send me your email address so that I can show you the pins I have as well as the chemicals and then you tell me how to go about it?
@@OwlTech333 OK, can't beat that... :-) I am just collecting stuff now and looking for ways, to process it efficiently with low waste and not much toxic fumes. One German guy uses HNO3 and H2O2 to get rid of base metals, looks like it works well, I just do not know, if it does not disolve gold aswell. Should not, but I have no practical experience yet,
سلام استاد در شروع کار 50gسیتریک اسید 10/ نیتریک اسید منظور ظرفیت نیتریکه یا برحسب درصد حجم متریاله درضمن بعد از این مرحله درشروع اکوئولوژیا لطفادرصد نیتریک وکلریدریک را میفرمائید وبعد از چکش کاری طلا درصد نیتریک اون را بفرمائید بسیار متشکرم استاد
I've done this hundreds of times and this is the first melting dish "explosion", from experience they аre quite resistant to thermal shocks. The dish was brand new, still hot from the borax glazing... @20:38 you can see a hairline crack on the right side of the crucible... maybe this is the culprit - a manufacturing defect...
I tried that too be when processing pins there's always some kind of contamination that I can't get out unless I melt into a button and process like in the video
@@OwlTech333 True. Lets not forget about the remaining 165g of pins that would yield more than 5kg of your average pins ;))) Congrats to that haul mate.
There's no way he got that much gold from that little amount of connectors. I have a bunch and will post my results when I process them. They are high yielding, the average pins are going to give you one gram of gold per pound of pins IMO. And this is about average for almost all gold-plated computer parts.
That would have taken you about 3 months to process that much and 55 grams is worth about $3,000 dont give up your day job because there are easier ways to make money
no offence taken, just because you haven't seen a crocodile it doesn't mean he won't eat you... Google РППМ 17-48, or even better ruclips.net/video/VjJP9BYkvU4/видео.html
I already did a search. There is only one article about this connectors in terms of gold content and this is on thebridgestudio.ru and another 2 or 3 sites (the same article). They are giving indeed a huge percentage of gold for this kind of connectors - max. 2.5%. But not 3.4%. In this case how reliable is only one source for information, wich is not even official? After that, why shold I make a connector with such a thick layer of gold wich is a soft metal and after few hundred cycles I'll remove it by scratch? And there are some other more reasons. Even I didn't saw the crocodile, I can use the common sense. Anyway, I wish you good luck.
Наука
dude... awsome return... thanks for bring us along
Thanks for watching!
Отменный результат!
Excellent result!
Спасибо!
It's almost like those pins were gold filled and nor plated.
Have a GREAT Day!!
If its multiples by kgs wow😍 awesome sir... I have been following ur videos.. Tried and got good result s..
Great result!!!!!
Thank you!
very nice and a lot of info, way to go. I noticed you must have access to plenty of the needed chemicals, some of which are hard or even impossible to get these days (i.e. HNO3). Hence my question, is it possible to achieve the same result using only the minimal amount of chemicals, for instance, you need a lot of de-NOx-ing product so perhaps it's possible to use less HNO3 to start with? Kind regards
How much aqua regia use to dissolved per gram metal/Precious metal ?
Congratulations excellent job !!!
Alex Carle Thank you!
WOW! That was an awesome yield from those hefty pins. Was there any silver recovered during these two processes? Love that deep orange colored liquid on the second refine!
Yes there was some silver too but got mixed with other silver chlorides so i don't know the exact amount
How did you happen to get ahold of these?
A while back I was experimenting to recover pin gold with sulfuric acid and an electric current, aqua regia, sulfamic acid and sodium metabisulfite and I did not get good results. I would like to test your method, but I want to ask you if you could give me your detailed procedure in writing so that I can understand it correctly and not fail again, I will greatly appreciate it, thank you very much, I have been your subscriber for years, I will continue to watch your videos, thank you ... .
Where can we get this gold plated product?
We need asupliers for this pins but a trusty one where where can found it
I need to find some of those pins 😂
Crap i hit "send" too fast.
Would a leech with iodine have worked in this case or was the plating too thick for that?
If the pins were mine I would have tried it... anyway there was a lot of solder which holds substantial amount of gold, gold that iodine can't reach
@@OwlTech333 Oh yeah. Its sad but of course you still need a HCL wash for one or two minutes with HCL before you use iodine or any other less harmful solution.
Yeah, the remaining solder is realy an issue ...
Great video really interesting 👍😎
Does anyone else get drunk and watch excellent refining videos?😁☝🎼🎶🎵🎹🔔
If you smelt the pins with borax, soda ash and silica + silver and lead. Then cupel it. What would be the result? Better or same?
Same I think
Adds extra unnecessary steps. A pinch of borax and pinch of soda ash is more than enough
Parabéns pelo resultado minerador.
What is the ratio of acids to make aqua regia?
How much is the concentration percentage (w/w) of HCl and HNO3 acids?
I've used 3HCl(32%) : 1HNO3(62%)
@@OwlTech333 I have HCl 32% and HNO3 68%, does these work?
@@sohaibal-arefi5397 yes
Show, parabéns 👍🇧🇷
Cho tôi hỏi lúc ngâm hno3+ 50g citric ngâm mấy h? How time và để vậy + hno3 vào ngâm tiếp hay rữa sạch rồi mới thêm hno3 vào anh? Trong bình bột xanh nó ra nhiều quá làm cách nào a
Bạn ở tỉnh nào
From where I can find these connectors ?
Soviet electronics
Excelente.
Why didn't you dissolve the gold powder in aqua regia instead of melting it then dissolving it in AR ?
Some contaminations are removed during melting
I have to say though... that is a GORGEOUS button
Thank you!
Hola... en la segunda precipitado.. lo hace con nitrato de sodio ? O con metabisulfito de sodio?
nitrito de sodio NaNO2
@@OwlTech333 tienes algún curso de refinado de metal?
Hello! If I mix citric acid with nitric acid, does it dissolve the iron faster without heating? Thanks!
Yes
@@OwlTech333 Thank you very much!
Just remember to use diluted acid
@@OwlTech333 All right! Thank you!
@@OwlTech333 I want to dissolve silver-plated iron. Will the citric acid not bother me if I want to polish the silver?
Sir! It's really awesome
Would you like to share full details about this process like purity of chemicals and quantity of chemicals kindly consider thiz comment tq so much sir :)
if 1kg pogo pins or banana plug pins how many grams of gold can be obtained?
I haven't processed any of them
@@OwlTech333 when do you process,? I will wait and want to know the result
Excellent have you got a list of the procedures 🍾🥂👏👏
Thanks, it's all in the video
@@OwlTech333 l must watch it again my fortune awaits 😁🍻
Fantastic video sir
Thanks
Hi! Can the golden plating be removed using nitric acid only, then get processed using aqua regia? Great job, by the way.
Yes
@@OwlTech333 Can you send me your email address so that I can show you the pins I have as well as the chemicals and then you tell me how to go about it?
@@OwlTech333 could you be able to provide email Id so that I could ask you some doubts 🙂
@@krishnanunnits9332 you can ask here
@@OwlTech333 bro where do you sell the gold you recovered
One more question: Why don't you use hydrogen peroxide with nitric acid to reduce NO2 and turn it into nitric acid again (saves nitric)?
I didn't have any
@@OwlTech333 OK, can't beat that... :-)
I am just collecting stuff now and looking for ways, to process it efficiently with low waste and not much toxic fumes. One German guy uses HNO3 and H2O2 to get rid of base metals, looks like it works well, I just do not know, if it does not disolve gold aswell. Should not, but I have no practical experience yet,
@@frantiseklaluch6605 It doesn't, I have tried it.
@@OwlTech333 thank you :-)
Super 👏👏👏
That's one big ass button you got there
WOW!
And how we test the purity of gold
specific gravity test?
Seriously though, wtf happened to that first melt dish?! Love those gold rocks!
Just a bad batch I guess because the same happened with another two
Can the same thing be done with vinaiger and salt,?
Not with the same success
@@OwlTech333 explain ; not with the same success?
Thanks for video. But why did you use citric acid
To get rid of lead and tin
@@mbykhanov Thank you
@@mbykhanov thank you bro
Спасибо было интересно, удачи вам.
Спасибо за просмотр!
Damn Man! You removed all those pins manually or any special secret ?
Hard manual labor
@@OwlTech333 damn
If I will provide you 1 KG Pins how much you can give me ?
Видео класс ,👍с меня лайк интересно посмотреть в таком количестве осождение спиртом или водкой очень красивое зрелище
Спасибо!
سلام استاد
استاددرصد دو اسید نیتریک وکلریدریک اکولوژیا رالطف میکنید البته وظیفه سابسکرایب را انجام دادیم متشکرم جواب دهید
Wicked brother, a monster nuget! Like.
What is the aqua regin
Aqua Regia HCl:HNO3 3:1
👍👍👍
Jast fery gooood
Thumbs Up
Why citric acid. Wont nitric do it
because of the tin
How much gold 1kg mix cpu pins boards
haven't tried them yet
@@OwlTech333 ok thanks sir
The Polish connector called LDB 32 pins has 0.9g of pure gold in one piece
I haven't encounter them yet
А можно теперь еще видео где вы тратите деньги, а то какое-то ощущение незавершенности )))
Привет,видео на 5+,👍
👍
👍👍👍👍👍👍💪💪💪
PROFI MAN
like #20
Where are you from?
Chanell says UK, you speak Russian, using Czech SIMAX glass...
Thats globalisation btch))))
سلام عليكم عندي ماء ملكي لايترسب ذهب كيف ترسيب الذهب
Copper
@@OwlTech333 تقصد السبب لايراسب ذهب من النحاس
@@OwlTech333 رسبت النحاس بل المنيوم
@@OwlTech333ولا يرسب ذهب
That is a yield of 3.4%!
После растворения припоя осадок на наличие золота не проверяли?
Все потом травил в ЦВ, осадок тоже.
@@OwlTech333 жаль на видео не попало. Как по русски smb ? Пиросульфит натрия?
Those Marxists weren't skimpy with the gold plating, wow!!
احسنت
А год какой разъёмов
Мишака Дудиков разные
Karat ?
24
Maaf Mohon penjelasan tertulis bahan kimia dan cara pengolahan dari tahap demi tahap terimakasih
gunakan subtitle
This gonna be good
سلام استاد در شروع کار 50gسیتریک اسید
10/ نیتریک اسید منظور ظرفیت نیتریکه یا برحسب درصد حجم متریاله درضمن بعد از این مرحله درشروع اکوئولوژیا لطفادرصد نیتریک
وکلریدریک را میفرمائید وبعد از چکش کاری طلا درصد نیتریک اون را بفرمائید بسیار متشکرم استاد
Откуда у тебя советские разъемы
случайно наткнулся ;)
@@OwlTech333 ха-ха,
Thermal shock is what broke the melting dish.
I've done this hundreds of times and this is the first melting dish "explosion", from experience they аre quite resistant to thermal shocks. The dish was brand new, still hot from the borax glazing... @20:38 you can see a hairline crack on the right side of the crucible... maybe this is the culprit - a manufacturing defect...
@@OwlTech333 that is it would take a small crack.
22:06 бура или сода?
бура
If you used less nitric at the start of your aqua Regia, you wouldn't have to expend so much excess nitric at the end.
correct
I want a subtitle
to understand
Comic very soon
1.65kgاز چند کیلو اسلات بدست امد
just go straight to the secong refining of the gold powder without melting it into a button first, saves gas and loads of time.
I tried that too be when processing pins there's always some kind of contamination that I can't get out unless I melt into a button and process like in the video
Неплохо. Но мне кажется что тут вес приувеличен.
Радиотехник вес щирый или вес золото?
@@OwlTech333 вес золота
Радиотехник прошлой раз из 1,5кг 50г золото VERY high yield GOLD plated pins ruclips.net/video/S3zWeALHwSg/видео.html
is pure gold real 24 carat gold?
Yes
@@OwlTech333 Where can I buy a scrap processor?
can you give a link ?
Holy cow!
55 GRAMS from 1,5 KG.
That's just plain insane.
Now i *have* to find out where i can find russian stuff and its all your fault!
1000 it's 1.65kg actually :)
@@OwlTech333 True. Lets not forget about the remaining 165g of pins that would yield more than 5kg of your average pins ;)))
Congrats to that haul mate.
One day you can melt all your buttons together to make the world's most valuable drink coaster.🍸
There's no way he got that much gold from that little amount of connectors. I have a bunch and will post my results when I process them.
They are high yielding, the average pins are going to give you one gram of gold per pound of pins IMO. And this is about average for almost all gold-plated computer parts.
Подписался, давай дружить каналами
سلام عليكم لايرسب ذهب عندي الماذا
I tried every known process but SMB never dropped gold.even from the richest solution from telecom boards.
Sir i,m Robiul sir give me SMB chemical
Na2S2O5
Show...
I like vidio coba bikin vidio new big bos
dommage trop de publicités. 3 en 5 minutes , c est trop
sodium metbisulfite SO2- IS A Deadly gas too, again don't play with that
That would have taken you about 3 months to process that much and 55 grams is worth about $3,000 dont give up your day job because there are easier ways to make money
Actually it took me 1 day to process from start to finish, but you are right about the day job, that's why this is only a hobby of mine.
Why not just enjoy the video instead of be comments like that it's interesting and that's wot counts
5.5g gold
Vilim Beros 55
@@OwlTech333 nice
@@OwlTech333 nice
No offence, but in my opinion is a fake. You simply cannot have 3.3% gold on those pins. In the past I had trust in what you said...
no offence taken, just because you haven't seen a crocodile it doesn't mean he won't eat you... Google РППМ 17-48, or even better ruclips.net/video/VjJP9BYkvU4/видео.html
I already did a search. There is only one article about this connectors in terms of gold content and this is on thebridgestudio.ru and another 2 or 3 sites (the same article). They are giving indeed a huge percentage of gold for this kind of connectors - max. 2.5%. But not 3.4%. In this case how reliable is only one source for information, wich is not even official? After that, why shold I make a connector with such a thick layer of gold wich is a soft metal and after few hundred cycles I'll remove it by scratch? And there are some other more reasons. Even I didn't saw the crocodile, I can use the common sense. Anyway, I wish you good luck.
Fake.
wanna bet?