That's how I've been melting too, wet from the beaker to the dish, why waste time drying it twice. Stays in the dish nicely without blowing out also. Thanks for the videos bro!
Here using ferrous sulphate and satisfying results, if using sodium metabolisulfate would the gold result be satisfying too? Because I once tried to use sodium metabolism but nothing satisfied with gold
For the initial step of removing other metals from the pins, when you mixed nitric acid with water 50/50, how long does that process take with 1.5kg of pins like you used?
@@OwlTech333 thankyou, and are you incrementally adding hydrochloric acid with a dropper to limit the use of a precipitant? What I'm asking is, Are you making Aqua Regia for this video? during the initial dissolution, was that just nitric acid and water? When I saw orange fumes I figured you were using aqua regia but then the gold would be mixed with the other metals right?
im curious as to how long this process took to achieve. as well would i be able to use this same process with the gold plated material i showed you. and are you using distilled water or regular tap water?
I know it has nothing to do with the video but how much gold can I expect to see out of 20 kilos of Pentium Pro cpus.? I'm looking to get into the bizz thank u dude
@@OwlTech333 Hello sir I have gold plated connectors/pins With 3 microns as gold plating thickness I want to know how I can refine gold from this Please all the process step by step Thank you
good job .i like your videos . may i aske u a qustion about sulfamic acid . what is the quantity needed to add to aquaregia ,or how we can make sure that the nitric is exusted frome the soulution
Dirty Gold wouldn't be 23k . 96... This gold wasn't refined at all, there's too many particulants amongst it. Don't get me wrong, I do like your videos, but I would like to see the clean up.
¿ Y como los tratas para poderte deshacer de ellos de forma segura ?, es importante tratar todos estos temas , pues luego la gente no sabe que hacer con los residuos. Gracias.
Los carbonatos pueden calcinarse para convertirlos en óxidos, y luego pueden usarse con hormigón. Más sobre el tema que puedes encontrar aquí: goldrefiningforum.com/~goldrefi/phpBB3/viewtopic.php?f=47&t=1300
@@OwlTech333 Hello I Hope You are well I found your mail adress on RUclips Please what is the thickness of gold plating if this pins/connectors ? please on 1 kilogram of pins and connectors gold plated with 1 μ(microns) How much is the average yield of gold in gramms Waiting for your Reply Thank you
OWL Tech, Why is it so hard for You people who post Your directions on RUclips for "everyone" to see/read, That You don't give equal directions for "HEATING TEMPERATURES, OR PERCENTAGES OF MIXTURES, OR "TIME OF PROCESSING" as if theres something wrong with how You do it???
I understand Your frustration, but this is not a "HOW TO" video. This a gold yield review on specific type of scrap. If need specific information regarding specific process, www.goldrefiningforum.com is the place to go. Most of the knowledge I possess was obtained there. I'm not a chemist. and if I can do it so can you. Word of advise if I may: there are no shortcuts and one size does not fit them all... Every reaction is unique due to the enormous number of variables involved.
@@OwlTech333 Thank you Sir, So very much!! I am a self-studier!!! So anything I feel I am able to do, I do with the intelligence God gave me. I am grateful, Most grateful for Your direction!!!
You will have a hard time getting specifics from anyone I'm a member of some dedicated forums to recovery's and scrapping people tend to guide you to literature and things first cautioning you to read through multiple times as people don't want to say do this and you do but a variable be off and an accident happens they don't want that on there conscience is what I've found also EVERY batch is different I may say I got x amount per x amount and i perhaps have but I'll never recreate that exact batch Never best to go with baseline numbers and when you get a great batch consider yourself blessed and be ready to be called a liar by those who dont know there butt from a hole in the ground hope that helps explain why I think it is this way be safe and blessed happy scrapping!
Holy amateur hour. This has gotta be the most ghetto little science lab set up I have ever seen. Do you even have the proper PPE? I never see gloves so I doubt the ventilation is up to speed.
Amateur - you got this right (never claimed the opposite), the "little science lab" (flattering, unless I failed to see the hidden irony) is a simple DIY fume hood which serves its purpose : namely carrying away the last traces of fumes (reduced to a minimum beforehand by the process employed). Ever crossed your mind you don't see gloves because they are invisible ?(google: wet work barrier cream, invisible gloves, gloves in a bottle and so on) I DOUBT it! :)
Where i can buy just pins?
So what purity is this Gold? Surely it's just between 10k - 14k. ?
23K 96.7% pure gold: ruclips.net/video/6IZnrURKpUo/видео.html
Where You can get that materias to process?
That's how I've been melting too, wet from the beaker to the dish, why waste time drying it twice. Stays in the dish nicely without blowing out also. Thanks for the videos bro!
Thank you
Were these magnetic pins or does that matter, does it matter what the base metal is
These were non magnetic pins and yes the base metal matters
Hi there fellow very nice one question does It gives you the same grams of gold if you do the sulfúric cel prosses reverse electroplating
Hi
Can one take the recycling of gold and other metals from electronic scrap as a way to make money
I'm sure anyone can do it
@@OwlTech333 thank you so much
@@OwlTech333I mean, is it economically viable in your opinion?
@@ameerabdalrahman2308 depends on one's refining and trading skills
Here using ferrous sulphate and satisfying results, if using sodium metabolisulfate would the gold result be satisfying too? Because I once tried to use sodium metabolism but nothing satisfied with gold
For the initial step of removing other metals from the pins, when you mixed nitric acid with water 50/50, how long does that process take with 1.5kg of pins like you used?
5-6h
@@OwlTech333 thankyou, and are you incrementally adding hydrochloric acid with a dropper to limit the use of a precipitant? What I'm asking is, Are you making Aqua Regia for this video? during the initial dissolution, was that just nitric acid and water? When I saw orange fumes I figured you were using aqua regia but then the gold would be mixed with the other metals right?
@@JimboS1ice999 @0:56 nitric and water, @10:10 digesting pins in aqua regia
@@OwlTech333 also what is the purity of the end product? what karat? if you don't mind me asking? if it's near 10k or 14k that's amazing.
@@JimboS1ice999 привет, какие 10 или 14 карат, конечно 24! Я думаю Сова не против.
im curious as to how long this process took to achieve. as well would i be able to use this same process with the gold plated material i showed you. and are you using distilled water or regular tap water?
Man put on some gloves ! 😱
How much cost for 1.5 kilograms gold plated pins .. I want to bay this screp gold plated pind . Plz reply must
look on ebay
Which is the best gold-plated pin?
-Contact Plating-
FULL GOLD FLASH
SELECTIVE GOLD
GOLD FLASH
AU OVER NI
FULL TIN
GOLD 0.8u"
GOLD 10u"
my brother i always do jewelery rabbis work i does two time try but some powder mlcc my gold eating my brother what can I do I don't no
Привет дружище, люблю твои видосы! Всего самого наилучшего! Да, Советы они такие)))
May I ask
What are the pins from?
what do you do with the biproducts of the solution after process is complete?
Thank you for uploading the video
Dude it's in description. Google rppm17-48-2 like in video description, it's a flat brown connector
How do you acquire such high grade gold pins?
Great job. What did the pins come out of?
Thanks! Google "РППМ17"
Mow much nitric you used?
3l
С титрами по интересней получилось,лайк и успехов в работе!!!
Спасибо!
+OwlTech пожалуйста):
I know it has nothing to do with the video but how much gold can I expect to see out of 20 kilos of Pentium Pro cpus.? I'm looking to get into the bizz thank u dude
Manuel Padilla Intel Pentium Pro 256k ruclips.net/p/PLLm8aBXzLPMMsJRYqxLdBK81JsF84J9kJ
what was the total weight of raw material to obtain this 1.5 kg of pins ?
248 connectors x 37.5g = 9.3kg ruclips.net/video/Azlo5BGaSPc/видео.html
@@OwlTech333
Hello sir
I have gold plated connectors/pins With 3 microns as gold plating thickness
I want to know how I can refine gold from this
Please all the process step by step
Thank you
Does It gives you the same amount of gold if you procces them in sulfúric acid reverse electroplating
I don't use sulphuric acid so I don't know the answer to your question
Thanks
This pins are from which electronics. Which connectors have this pins
google "рппм17-48-3"
good job .i like your videos .
may i aske u a qustion about sulfamic acid . what is the quantity needed to add to aquaregia ,or how we can make sure that the nitric is exusted frome the soulution
Thanks! I add it while solution is still hot, in small increments with stirring ,until it stops fizzing.
Wonderful video but tell me how many carats a caliber
what brand of processor is that?
extract this pins from where.cisco and high telecom borad .or any kind of pins.?
РППМ17
you put the haet under the flask? or the bubble make in natural mode??
heat under the flask
Boz, for the second process, use aqua regia .thank you
I did ruclips.net/video/6IZnrURKpUo/видео.html
Профиноализм всё на пять с плюсом.Нам только от вас и учиться
Спасибо!
Exactly how much gold is in one kilogram of pins?
about 33.3g pure gold
@@OwlTech333 where i can get of this pins?
Здорово ,да очень жирненькие разьемы красиво ,молодец!!
What was the base metal
brass
@@OwlTech333 thank you so much for all your help it is much appreciated
Were these pins fully plated or partially?
William Bennett fully plated
Care to help me out checking mine out? How could I get some pics over to you?
And for pins like this that have some solder on them should i use hcl to remove them rinse and do 50/50 nitric acid
you can boil them in dilute nitric 1/10 H20 to remove the solder
51 grams from 1 kg of gold plated pins? If that's the case consider me rich
So you have many kilograms of RPPM pins? if that’s the case I consider you rich!
@@OwlTech333 ❤️
عاشت يدك اخي العزيز
Dirty Gold wouldn't be 23k . 96... This gold wasn't refined at all, there's too many particulants amongst it. Don't get me wrong, I do like your videos, but I would like to see the clean up.
this is the refining part: ruclips.net/video/6IZnrURKpUo/видео.html
@@OwlTech333 Nice video of the clean up 🤟🏼 That is what I like to see 👍🏼
Where did you get the pins?
Can you use sulfamic acid vs parasulfamic acid?
I am using sulfamic acid
Superbe !
Dans ton acide nitrique est qu'il y a avec le cuivre de l'argent ?
l'acide sulfamique combien de % ?
Merci!
Oui! Cuivre, étain et de l'argent.
J'ajoute de l'acide sulfamique en petites quantités jusqu'à ce que la solution cesse de pétiller.
Hi sir this is my same try not success why reason
Hola howltech es 1.5kg o 15kg disculpa la molestias y buen video
1.5kg 1500g
Привет... сможешь объяснить почему тут не использовал йод ?
Hola OwlTech , ¿ Que haces con los ácidos ? , ¿ como te deshaces de ellos ?.
¡Hola! Depende del ácido pero en general: neutralización y precipitación de carbonatos con carbonato de sodio
¿ Pero se pueden tirar por un desagüe sin resultados nefastos para el medio ambiente ?
¡NO! Necesitan ser tratados más
¿ Y como los tratas para poderte deshacer de ellos de forma segura ?, es importante tratar todos estos temas , pues luego la gente no sabe que hacer con los residuos. Gracias.
Los carbonatos pueden calcinarse para convertirlos en óxidos, y luego pueden usarse con hormigón. Más sobre el tema que puedes encontrar aquí: goldrefiningforum.com/~goldrefi/phpBB3/viewtopic.php?f=47&t=1300
What are these pins..are these from CPU?
old electronics 70-80's
Dear sir could i buy from ebay?
I suppose so
how to get Gold from solder
1 kg gold pollisig AR full process timing sir please tell me
What is the base metal?
@@OwlTech333
Hello
I Hope You are well
I found your mail adress on RUclips
Please what is the thickness of gold plating if this pins/connectors ?
please on 1 kilogram of pins and connectors gold plated with 1 μ(microns)
How much is the average yield of gold in gramms
Waiting for your Reply
Thank you
Awesome narration, you are a natural.
I hope the process became understandable, if not, I will be happy to shed more light on the subject
What narration ?
Maby there was a problem with the sound.
ahoj jsi z česka?
Ahoj! Ne nejsem.
@@OwlTech333 a odkud? umíš česky?
Do You Boiling That's Nitric Acid..?
yes diluted nitric
How Many Karat, Before You refining to 24k..? Oh Sorry. Im From Indonesian, It's Hard For Me To Speak English.. btw thanks For This Tutorial..
around 23.2K
really? 51g gold from 1500g connectors? supeeer
Awesome !!!
this is speaker terminal pin?
no, these are pins from old very connectors.
Couldn't be speaker pins. There's no speaking.
Very good, nice
Thanks!
what you add on 11:18 sec ?
sulphamic acid
THNX BRO... PUT ORIGINAL VOICE :)
berapa harga pin emas per kg??
Uau parabéns pelo resultado dom; bonito.
أين الفيديو الثاني
ruclips.net/video/6IZnrURKpUo/видео.html
فيديو رائع
Привет у тебя класные работы
Спасибо большое
krasav4ik,lu4shiy v etom dele!
Спасибо!
na etot obem ubajaemiy esli delat ceanidniy rastvor ushlo bi grama 2-3 samoe bolshoe. cena 3 centa nashix Evropeyskix,da i bistree budet. nalivaesh lij bi nakrilo i 4erez 4asik slivaesh,ostavlyaesh dishat material,jret na vozduxe o4en bistro...tipa ku4nogo vis4ela4evanya
Merci pour l'explication .
1 hours complete process complete
OWL Tech, Why is it so hard for You people who post Your directions on RUclips for "everyone" to see/read, That You don't give equal directions for "HEATING TEMPERATURES, OR PERCENTAGES OF MIXTURES, OR "TIME OF PROCESSING" as if theres something wrong with how You do it???
I understand Your frustration, but this is not a "HOW TO" video. This a gold yield review on specific type of scrap. If need specific information regarding specific process, www.goldrefiningforum.com is the place to go. Most of the knowledge I possess was obtained there. I'm not a chemist. and if I can do it so can you. Word of advise if I may: there are no shortcuts and one size does not fit them all... Every reaction is unique due to the enormous number of variables involved.
@@OwlTech333 Thank you Sir, So very much!! I am a self-studier!!! So anything I feel I am able to do, I do with the intelligence God gave me. I am grateful, Most grateful for Your direction!!!
You will have a hard time getting specifics from anyone I'm a member of some dedicated forums to recovery's and scrapping people tend to guide you to literature and things first cautioning you to read through multiple times as people don't want to say do this and you do but a variable be off and an accident happens they don't want that on there conscience is what I've found also EVERY batch is different I may say I got x amount per x amount and i perhaps have but I'll never recreate that exact batch Never best to go with baseline numbers and when you get a great batch consider yourself blessed and be ready to be called a liar by those who dont know there butt from a hole in the ground hope that helps explain why I think it is this way be safe and blessed happy scrapping!
Does it wrong makes m.
👍👍👍👍👍
👍👍👌
Sir sulphamic acid and SMB salt package photo please sir
Na2s2o5farmula smb
Wauuu
Все супер
hilo amigo
Like 👏👏👏👏
🖒🖒🖒 лайк
Does anybody want to bet me that this is either a Southeast Pacific or Indian people
English no hindi
Are shukar manao english hai,,,chineez nahi hai😁😁
Holy amateur hour. This has gotta be the most ghetto little science lab set up I have ever seen. Do you even have the proper PPE? I never see gloves so I doubt the ventilation is up to speed.
Amateur - you got this right (never claimed the opposite), the "little science lab" (flattering, unless I failed to see the hidden irony) is a simple DIY fume hood which serves its purpose : namely carrying away the last traces of fumes (reduced to a minimum beforehand by the process employed). Ever crossed your mind you don't see gloves because they are invisible ?(google: wet work barrier cream, invisible gloves, gloves in a bottle and so on) I DOUBT it! :)
@@OwlTech333 🤔🤔🤔...gloves in a bottle....sulfamic converts nitric to sulpheric...you NEVER dissapoint with lil gems of knowlage owl😎
sad attempt at copying another better utuber
فيديو رائع
Thank you so much!!!