Looking good mate. I'm having some issues with some of my slabs not adhering in certain areas. Plenty of slurry on slabs and sbr and plastersiser on the mix also. Seems to be in corners but I've laid slabs dry first a few times to get the correct heigh etc etc. Any ideas mate ?? X
But it’s perfect absaloutly spot on when it’s wet it becomes a problem for many reasons, it has no compressive strength for a staters then the mineral deposits from wet mortar is a nightmare and of course it’s to biscuit like in horizon which is simply poo, but once again thank you your feed back is always helpful for a few
![COLOMBIA vs. CHILE [4-0] | RESUMEN | ELIMINATORIAS SUDAMERICANAS | FECHA 10](http://i.ytimg.com/vi/TDjN4W3yy1k/mqdefault.jpg)
Love the attention to detail ❤
@@malcolmswann7223 thank you
@@malcolmswann7223 how are you
Beautiful. I still don't understand the dry mix theory... It just doesn't seem right that it will dry solid. Great job!
It needs to be a bit moist
Looking good mate. I'm having some issues with some of my slabs not adhering in certain areas. Plenty of slurry on slabs and sbr and plastersiser on the mix also. Seems to be in corners but I've laid slabs dry first a few times to get the correct heigh etc etc. Any ideas mate ?? X
Give us a call Ali Mate
@@GreentopLandscapes hello mate. When's best for you ? X
Tomoz mate I just got in
@@GreentopLandscapes no worries mate. Same here. Rest up x
How did you get this resolved mate?
No reason to use dry mix porcelain is not porous like the sedimentary stones, you're just adding extra risk of not adhering properly.
The screed mix has compressive strength and wont be biscuit like mortar plus we use a good Priming Slurry
You would rather have the mix slighlty dry then wet which is a nightmare as conpressinng and leveling bscomes hardwe as moisuriee leaves the mix
The reason for this is that it has compressive strength as when it’s wet it does not have compressive strength as liquid is not compressive
Mix is to dry
It was a bit hot I agree thanks for your feedback Mark
But it’s perfect absaloutly spot on when it’s wet it becomes a problem for many reasons, it has no compressive strength for a staters then the mineral deposits from wet mortar is a nightmare and of course it’s to biscuit like in horizon which is simply poo, but once again thank you your feed back is always helpful for a few