Which Size Stick Welding Electrode Is Best?
HTML-код
- Опубликовано: 27 июн 2022
- Big ones, small ones, something in between? Let's find out!
Learn to weld in small, simple steps:
courses.timwelds.com
Things I use for stick welding:
HTP Inverarc 160+ (awesome machine): usaweld.com/products/htp-inve...
Budget Friendly DekoPro Welder: amzn.to/3aFUQXW
Awesome Chipping Hammer: amzn.to/3H8hYdL
Comfortable Welding Jacket: amzn.to/39ckbIV
Switchable Welding Magnets: amzn.to/3zoF5z3
(These are affiliate links which provide a small commission to support the channel at no cost to you)
Discount code 'TIMWELDS' saves friends of the channel:
5% off HTP machines and quality accessories at usaweld.com
10% off welding coupons, kits and supplies at weldmetalsonline.com
5% off Evolution power tools at store.evolutionpowertools.com 
Наука
I don't know how you come up with your video ideas but I have found many welding searches I have done one of your videos pops up. I am always glad when it does because your videos are always informative and have no fluff or filler. Just a video that delivers what it promises in a timely matter for the subject being covered. Thanks Tim keep up the great work.
I second this comment!❤
Tim, I always come back to your videos when I'm practicing, stumped by a stick welding issue, or just generally need some insight on best practices. I sure appreciate what you do.
Tim, I cannot express properly through a RUclips comment how thankful and appreciative I am for your time and effort in making these videos. I've been learning to weld from scratch and your videos have made my learning possible. I'm finding new joy in life building with metal. The time you've taken to share your knowledge has changed my life in a very real and significant way. I never had a "shop" class in school, so your videos give me the gift of "access". I try to pass on the access by educating others and lending tools.
Thank you for investing your time in these videos. I'm looking forward to subscribing to your classes when I have the money for it.
I'm in the same boat, learning off my grandpa's old 225 ac stick.
As someone who's brand-new to this stuff, I bought the courses to help out while I'm taking classes for it, and they've been super helpful, especially since you went to the trouble to put all the notes with them. So....thanks!! :)
Good Job Tim 👍🏼Your videos are great, they get to the point and no bullshit.
Other welding videos are too complicated, too much info lost and confused.
Another great one Tim . . . very good video shots and explanation. You are the Man Sir . . . appreciate you so much!
Fantastic video I’ve been wanting to give stick welding ago for a long time and I’ve all ways wondered about the size of the electrode and the difference in them welding wise. Big thanks and great work 👍
This video couldn’t have at a better time! Will be buying your courses soon!
You're awesome, man! I bought a stick welder ($60) on Monday and have been gobbling up your videos.
My welds look like absolute ass but they're 300% better on Wednesday than Monday. I'm so dorked about this. It seems like freaking magic that any of it works.
Nice work! It's so fun, you're going to be hooked.
thats actually really interesting, i started with mig but ive gotten to run quite a bit of 6013 around the shop the last few months, i always assumed smaller rod for thinner material bigger rod for thicker, good to know that those small rods get just about the same penetration and gives me a better appreciation for how important amp settings are. when i first started with stick i would crank it to whatever the max setting for the rod was and leave it there for uphill, downhill, flat and overhead. if i blew a hole in something id switch to my mig and think that you just cant weld something that thin with stick, after a month or so i got it dialed in and i can tell just how big a difference there is between 80 and 90 amps etc. being self taugh can be a bitch sometimes but your videos really help, i was stuck on up hill welding up until just about a week ago where i found your video talking about rod angle, got my first half way decent uphill the next day.
Thanks for the lesson!
Very helpful, clear and to the point, great comparison and info thank you.
Great information, thanks Tim.
Very professional work!
Hi mate,
You just answered my questions
To use small rods for thicker piece of metal
Thank you so much for your time to explain
Great video with excellent content, thanks.
Good video, good explanation.
I was an apprentice welder, and certified as a journeyman the first time with a 7018 in the 6G position. That being said, it is a challenge to carry a larger amount of metal in a vertical weld.
I use smaller rod for the root pass because I can get it in closer then bigger rod for the cover/fill passes.
my old lincoln electrode welding lesson book uses 5/32 6010 to weld even thin metal like .125
I’m from the the UK that uses the metric system but I’d say the 1/8” / 10 gauge (3.2mm) because it’s the best positional rod & the most chosen size for using to put a root in with most pipe sizes
You’re coming up with a lot of videos as of late. That’s nice to see.
Great idea to translate dimensions in metric system. Very useful for an european! Thanks.
All the welds where good, you might of liked a larger size but each weld had a good spead and bite.
There's a good depth of fusion, it's doing it's job, you have to get the mass in the joint an have a good joint plan.
Great info!
Great info thanks
Your video was very helpful tthank u for explaining how stick welding work I notice it's 3 different size with different #s on it plus I see the difference from all 3 tho 💪💪💪💪
Very informative video Tim 👍I always switch over to stick from mig if I know the weld is going to be ground down, (I hate doing it but is a necessary evil 😈 sometimes fabricating smokers) due to the higher penetration.
😂Question..
The stick welding course only
Anyway I am Oldman and a professional commercial handyman..but I learn slow..
There are quite a few lessons offered.. in the stick only classes. Can I rewatch a lesson as many times as it takes to get pass my thick brain..?
Thank you
Richard 🎉
Thanks✌😎
Hi Tim! Would it be possible for you to review 7014 rod? I am especially interested in its ability to tack weld and I am interested to see how it would perform on sheet metal. Thanks!
Excellent video and amazing presentation! Just one comment on the classification. They don't need the "R". Instead of ER7018 use E7018.
Depends on the application
Oven cleaner works well too, for penetrations tests.
Cant beat AC for running large dia rods especially on heavy materials in position. Back in my shipyard days I knew some guys who were wizard's using 5.0mm mild steel rods on vertical butts ,fillets and overhead butts and fillets
Excellent 🙏🏼
so interesting .Question do electrode packages have a recomended starting amperage on them that you can fine tune into the material your welding. or where is there a chart ? egsample a 7018 rod is between70 or 80 amps say ? I have a big gas welder from auction but just a guess and by golly welder .my electrodes are all in the plastic storage tubes from previous owner.
Cool video
Very helpful vidio nice sir
Before your video, I was wondering if I made a mistake about 4mm rods it's 6013 but I think considering your explanation I think it's really fine now. My welding surface is 3mm and 6 mm usually and go up to 18mm for flanges
If the pieces are welded together, why is penetration a concern in the Tee joint? If I was gluing parts together or soldering parts together I can see that a larger connection area would give more adhesion force. But since the weld fuses material, unless the filler material has lower tensile strength than the base metal, why would penetration matter. Wouldn't the size of the weld determine the strength the joint, so the rod that can give the weld size needed the be what is important in determining which size rod to use?
Good god that looks better that what I’m laying down
But i do have a {old school) 225 ac Lincoln i will be firing up in a few days just waiting for a part and we see how that works on these stubborn rods.
I love the video. One interesting point you bring up is the engineering aspect of it. I know it's a specialization in itself but perhaps you could make a video either by yourself or invite an engineer to talk general rules of thumb for DIY-ers. For example as a learning home welder I have no intuition if these welds you've shown on the thick plate, if they are ok or not. Your conclusion is that you can use tha smaller electrode on thick stock - I couldn't make that as a DIY. Probably need to find a good welding book as well :)
What stick for 4.8 i think is 3/16ths square tubing im going to use the Azzuno Amazon welder to finish welding this 3/16 steel tubing for a utility trailer.
Hello can 220v maxmeck welding machine weld 7018
where do you recommend looking for good quality electrodes? i am new to stick welding. got some electrodes at harbor freight but not sure if they are poor quality or i am just not very skilled yet!
Are all stick welding rod the same length? What is that length? I can't seem to find any info on this.
Thanks Tim jimmy Aust
How to weld eutectic + castolin xuper 6055
Is it possible to weld through slag-holes? they are too tiny to be ground out without spoiling the workpiece.
No luck my 6011 or 7018 rods wont weld they keep sticking and burning up....am i not kicking out enough amps or to much i just cant figure it out...but 6013s burn great between 70 to 80 amps... what do i do ?
With a 1/8 rod, you can control it better specially on vertical up
The best rod is the rod that suits the job.
more passes increases heat input and warpage
Hi sir am from the Philippines and I am doing some DIY stuff and a beginner when it comes to welding. ..i would like to ask the best size of rod for a 1.5mm thick metal and the right amper
Thank you and I hope you can see this comment..
Godbess more power to your chanel
Could this be why I don't have any penetration on my 8mm material fillet welds with 3.2mm 7018 rods? I have been trying everything but once the weld has been ground flush I can see it's not penetrated much at all and a small hammer is all that's needed.
mostly you cant penetrate deeper than 2mm no matter which electrode. so you have to make a v notch
Tim, I have a 90amp stick welder to start learning small... Which rods fit best for this size welder?
3/32
Could you do a video on voltage? I see everywhere talking about amperage but if my highschool knowledge doesn't fail me, the power is totally dependent on voltage too, and the same manufacturer have different voltages for different machines. Mine is 59V so technically even the ballpark you advise should be adjusted. Am I missing something?
I think stick welders use 120 or 240 volts and you adjust the amps accordingly,,on mig welders you can adjust the volts but its usually nowhere near 120.
@@slamdunk6170 sorry if I was not clear, I mean voltage output (usually DC) not input (AC)
How many amps is your welder pulling from the wall?
As an electrician/"barn-yard welder" I once measured stick current with my clamp-on ammeter and it matched the selected current on my Craftsman "transformer" welder. The 240V supply current measured proportional to the selected welding current. So figure if you select the maximum rated weld current (220A) the welder will draw its full rated 50A from the wall. So 110A welding current would draw 25A from the wall. 70A will draw about 16A from the wall.
If you have a 120V "stick" welder, you can double the above wall-supplied currents for the same welding currents. So the maximum welding current you can expect from a 120V "transformer" welder would be 2.2 x 20A = 44A before tripping the house breaker. Not very useful for general metal shop work but maybe enough for "hobby" sheet metal work. Given that most welders have a duty cycle limit for higher welding currents, and circuit breakers take a minute or more to trip at their rated current, you could probably push the weld currents a bit higher in short bursts of usage at either supply voltage. I'm guessing that you could get more available and usable welding current from a "modern" "inverter" welder (the newer smaller ones that weigh about 1/4 of an older "transformer" welder).
If you use "the wife's" 30A 240V dryer outlet for your occasional welding you will be limited to about 120A welding current before tripping the "house" breaker. This has often proven enough capacity for the renter, small shop and "barnyard" occasional welder.
Obviously its hard to beat a fully equipped shop if you are lucky enough to have one.
This is limited experience. If others have better information, feel free to comment.
Doesn't that depend on the thickness and make-up of the material being welded
Remember people, 120volt amazon welders are rated for 1/16th rods! I've found 6011 1/16 rods to work best for general home purposes.
I just welded 1/4” plates with 6013 rods at 55amps using my 12v yesswelder 160 . And this is my first welder
👍
I tend to find 1/8 inch rods produce more pretty beads
1/4" is better
👏🏻
glad it missed your eye
On your well why don’t you bring it when you almost get to the end bring it back into the world and circle it and pull it out
What hit you in the face buddy?
Wife
What happened to your face in this video?
No offence but you should have started with the larger electrode first just because the material was cold and you used the smallest rod at the lowest amperage first so the smaller let rose is getting robbed on the penetration lol
Every time he says "3-30 seconds of a inch" I cry in metric....
Excellent 🙏🏼
👍