Hi everyone. when lowering gold from aqua regia with SMB, it is lowered with gold and lead/tin. (gray white precipitate) how to get rid of it? help please
The tin should be removed long before you actually drop the gold with smb. However since your already at this point tin can be removed by boiling in HCL. As for the lead before dropping you gold add a small amount of sulfuric acid this will drop the lead and it can be filtered. Denoxing with sulfamic acid instead of urea will accomplish the same thing. At this point with tin and lead in for gold powder boil in HCL. Then redissolve everything in AR and add some sulfuric acid and filter. Then drop gold again.
You chanel is demonetased, sory to hear that brother. You must contact RUclips and ask for the reason for demonetasetion! If old music is from RUclips create list, i think that is not reason!
Had 6 grams blow up in my face when pouring into a cold mold, spent a few hours picking up tiny gold beads out of the concrete floor, good to learn from others mistakes😉
👍Чотка!😀С воздухом побыстрее окисляется наверно.Флюсы можно попробывать ещё,с серы начать к примеру,натриевая,каливая силитра,сульфат натрия...и пожиже расплав будет и могут почти всё окислить и растворить😀вот как поведут с железом хрен его знает
ne disite parami svinta.svinet iz organizma pociti ne vivoditsea.a potom nacinaetsea onemenie konecinostei i vseo takoe....pocitaite simptomi otravleniem svinta.a za trudi Laikos.
You are indeed the best processor sir at 11:30 PM Make Memories Get 24K Gold 😁😁🤣 Thank you for making a 24k gold process video tutorial 👍👍👍
Sir, I love watching your videos. please can you write the model number of the transistors?
From where I can find those transistors??
Доброго. Таки вопрос. А кальцинированная сода пойдет или обязательно каустическая? Какой Ph нужен для щавелевой кислоты?
кальцинированная сода тоже пойдет pH 3-4
@@OwlTech333 спасибо.
Сколько энергоносителей потратили? Газ, уголь, электричество...
Hi everyone. when lowering gold from aqua regia with SMB, it is lowered with gold and lead/tin. (gray white precipitate) how to get rid of it? help please
The tin should be removed long before you actually drop the gold with smb. However since your already at this point tin can be removed by boiling in HCL. As for the lead before dropping you gold add a small amount of sulfuric acid this will drop the lead and it can be filtered. Denoxing with sulfamic acid instead of urea will accomplish the same thing. At this point with tin and lead in for gold powder boil in HCL. Then redissolve everything in AR and add some sulfuric acid and filter. Then drop gold again.
23:40 Good thing the gold was not in powdered form. That sponge really held together. Thank You for showing your mistakes. I learn from them.
Was it just gold and copper in dore or silver in it too
Burn Roe silver and gold, no copper present
Nice . i usually have copper left with that kind of material i guess it oxidized of in cupell
Correct
Busted up new unused transistors. What a waste.
Love the music brotheer. This video is soo cool mate!
999 Dusan thanks I had to compose new music because the old one was used in too many videos which I believe caused the demonetisation of my Chanel
You chanel is demonetased, sory to hear that brother. You must contact RUclips and ask for the reason for demonetasetion! If old music is from RUclips create list, i think that is not reason!
No, I made the music and everything on my videos.
Please have a white deposit problem and no problem?
how do u clean the gold botton? i mean getting rid of borax.
Arnold Kabayo boiling In dilute hydrochloric acid
@@OwlTech333 wow thank you so much.. this really helps me a lot.
Ah, the sound of your crucible cooling down as you look at your final yield. My favorite part of the process!
Лайк ...как вы считаете -- добавлять селитру для быстрейшего обращения свинца в шлак , это нормально ??
да, получится, только не знаю если потери не будет
Wonderful video nice sir How do you separate the Tourister cap
Nice vedio.
Gold & PM refining process Hassan thank you
Спасибо за видео, было очень интересно, лайк и удачи вам.
Спасибо за просмотр!
Is this Technique better then SMB Technique ??
Yes but yields are not as great but the amount you save on chemo is well worth it.
We can use aqua regia or no?
hassina belala use it for what?
Banging tune😎
nice job sir not counting dropping out material from crucible lol but that happened sometimes once i drop 2g of powder on my messy floor lol 👍👍👍
Real bro?
Yes
Hi sir how are you and new videos upload sir
The music is sooo annoying
Had 6 grams blow up in my face when pouring into a cold mold, spent a few hours picking up tiny gold beads out of the concrete floor, good to learn from others mistakes😉
R.I.P.
За обзор, методу и выхлоп👍45+
Франсузкий на порядок выше) 24:01)
Buen video Owltech :D
не плохой слиточек злата вышел!) лайк!)
*👍Very good*
Это хороший результат , так как много было без жёлтого донышка
Definitly anybody dosnt buy this goods in Turkey! Because of this Gold not single color " mistake Gold "
This one was 99.99 in Turkey 995 is enough
@@OwlTech333 No broather! This material is whit irridium min 8 or 10 ppm! Can you understand me? Anybody doesnt buy this goods! İRİDİUM metals !!!
Also you are right! Your goods is %99,9
@@oltabalk1047 iridium in the transistors?
@@OwlTech333 No! Your tehcnics and metots are prof and perfect... Your golds are 99,9 and dont look me! There is İridium in a lot of CPU
👍Чотка!😀С воздухом побыстрее окисляется наверно.Флюсы можно попробывать ещё,с серы начать к примеру,натриевая,каливая силитра,сульфат натрия...и пожиже расплав будет и могут почти всё окислить и растворить😀вот как поведут с железом хрен его знает
Лайк и просмотр!
ne disite parami svinta.svinet iz organizma pociti ne vivoditsea.a potom nacinaetsea onemenie konecinostei i vseo takoe....pocitaite simptomi otravleniem svinta.a za trudi Laikos.
this USSR transistors
most of them yes
не думал что так мало думал 30 выйдет
Vladimir Fomenko если все были хорошие 15-20гр. Au max
красота!!! Лайк!!!
👍👍
👍👍👍
👍