I love your videos and watch them often. I've been doing stained glass for two and a half years now but have only down stained glass mirrors and tables etc with grout lines instead of solder line. Im just getting into using copper foil and solder and love your work. I just had a cople of questions: what size of lead came do you use around the edge of the panel as well what size do you twist to make your decorative edge and is it u came or h came?
Steve. . . How do you manage to NOT melt the lead came while you add the solder??? No matter how I try I always seem to burn through and melt my came. Any suggestions will be appreciated. Thanks.
You are a most excellent teacher...thanks!
Thank you so much for all the teaching you have giving me ,its such a pleasure watching your video.
They don’t sell Canfield in Canada
Patricia
I love your videos and watch them often. I've been doing stained glass for two and a half years now but have only down stained glass mirrors and tables etc with grout lines instead of solder line. Im just getting into using copper foil and solder and love your work. I just had a cople of questions: what size of lead came do you use around the edge of the panel as well what size do you twist to make your decorative edge and is it u came or h came?
Are you attaching the lead to zinc, tinned foil or 'U'?
Steve. . . How do you manage to NOT melt the lead came while you add the solder??? No matter how I try I always seem to burn through and melt my came. Any suggestions will be appreciated. Thanks.