Flexible 3D Printing Filaments Tested - Which Flex is Best?
HTML-код
- Опубликовано: 12 июл 2017
- There is LOADS of flexible 3D Printing filaments on the market today, all with different properties and features. In this video we'll put 6 different brands to the test.
Octopus model used in this video -
www.thingiverse.com/thing:8896
Filaments tested (in order of appearance):
PolyMaker PolyFlex - www.polymaker.com/shop/polyflex/
Generic TPU (3D Printer Gear) - www.3dprintergear.com.au/51-f...
Fiberlogy Fiberflex 40D - fiberlogy.com/en/fiberlogy-fil...
Essentium TPU - essentiummaterials.com/product...
MakeShaper TPU 85A - www.makeshaper.com/product-cat...
Diabase X60 Ultra-Flexible Filament - flexionextruder.com/shop/x60-...
NOTE: No links above are affiliate, no money has changed hands and all opinions in this video are my own!
50 3D Printer Tips and Tricks eBook - gumroad.com/l/QWAh
Like what we do?
Visit us at makersmuse.com for more information about Makers Muse!
Say G'day to us on Twitter and Instagram @makersmuse
Ways you can support Maker's Muse:
- Want to buy a 3D Printer but don't know where to start? Get our eBook here!
gumroad.com/products/NBvg/
- Support us on Patreon
www.patreon.com/makersmuse?ty=h
- Buy a T-shirt!
www.redbubble.com/people/maker...
- By using our amazon affiliate links
US - amzn.to/1Ym50j1
UK - amzn.to/1PJICdR
Or a direct donation through RUclips
And lastly, a BIG thanks to the community, and those who have supported us here at Makers Muse!
---- Наука
weird flex but ok
I clicked only because I knew you'd be there
I'm disappointed there was no Flex tape in the vid. :(
Ahhhhhhhhhhhhhhh ☝️
I see what you did there. Well played.
heh
A bit disapointed that there is no Filaflex or Ninjaflex, but great video
true, but don't see it much in Aus. Maybe it'll be in a part 2.
Maker's Muse May i suggest that you also test Semiflex ? So that you can compare what you call semi-flexible materials to what is considered by manufacturers "semi-flexible"
Cheeta from ninjaflex seems interesting.
Ola Ruud I have used cheetah filament and it's amazing. Printed at 60mm/s and it worked perfectly. very flexible and fast. No jams or anything. Just a very expensive filament lol
Carter Bridges I like Cheetah also much, easy and fast, good quality, won't buy basic TPU anymore
Thanks for including us! Glad to see you had good results!
Nice to see an old vid, helps me recognize how much your presentation has improved over the years while still maintaining quality content.
what are the odds that I've been watching a ton of videos on this topic and you put out this video! Sweet!
Thanks for the hint with Fiberlogy. I’m looking to start a 3D adventure with Select Mini V2 and currently I’m exploring filament pricing, availability and reviews doing first 3D models to see if I should really jump in. Anyway I really like your videos, good work!
Great review! I'm printing usable shoes from TPU and TPE, your video is a nice addition to the materials I need to try! Thanks!
Hey Angus, your videos are always top-tier quality and the perfect mix of entertaining and informative. I get excited about any content that comes from you. Keep up the good work
first
Thats cheating!
Maker's Muse not fair
:P I did it after making it public! But no, not fair hehe
wow i wanted to be first :(
Maker's Muse i have a question can you do a review on a printer called the cube 3 from 3d systems please
This was great. I was looking for a more rigid filament and had no idea where to find it. Now I have some options.
Such a dope video man!!! I have been looking up flexible material !!!
this is the EXACT video i needed
I just love your channel every time I have a doubt. I just search for your videos and I find all the answers I need ^^'
Congratulations! I'm your fan. kkkk
and I'm glad that even though I'm Brazilian I learned English and I can understand your videos normally
Thanks man. I got my first spool of TPU and had a hard time printing larger objects. Your hint with increased temperature, lowered speed and no retraction did it on my ender-3
but did the stringing increase after you disabled retraction?
You should do an update on the last filament. Like changing the settings so it prints well and printing (or even designing) some useful things would be great
Awesome! SO glad you had the X60 on here! I am getting a product prototype done using a 60A TPU 3D printed. I should have it by Feb 10th. I have it on 100% infill so I hope it doesnt under extrude at all.
Thank you for actualy making a helpful video, i have been having trouble finding somthing useful untill now.
I like the new energy, keep it up
Great video. I blindly bought nijaflex and it is elastic and combined with the fact that it stuck to itself on the roll a little bit I was unable to print on my Cetus(under extrusion). Now I have a guide I can use to determine which brand to go with, thanks!
i love it when he says "LETS GET STARTED"
Nice to see original content & not just reviews on the CR10 & drones.
Thanks for sharing :-)
Good introduction of this tricky prints :-)
While this is an older video, I have just bought & tried a roll of Polymaker TPU90. (purchased locally here in Oz) This is the softest filament I have tried to date & have been very impressed. Yes a few little tweaks for my Prusa & though it's too soft for some things, so far I have found it to be of very good quality.
SUPER HELPFUL!
Great video. Thanks man!
Thank you for pointing out flex vs elastic
the pink is so gorgeous! also I feel so lucky because I at print 40mm/s with my anycubic i3 mega-s and never had an issue :D I use retractions and a linear advance value of 0.65 (normally 0.4)
Extremely useful information. Working with developing prosthetics and was wondering if as in the case of finger tips for instance which of these appear more able to grip or tackiness, not just the durometer.
Life with a 3D printer: Currently 6 A:M. Started 45 minute print at midnight. Just finished now. Dealing with the design, misprints then a huge clog was well worth it.
Hendryck De Los Santos what did you make
I made Arduino clips to hold and mount an Arduino board to anything by screwing the mount in, but I'm new to 3D printing which explains the long hours I put into printing something so simple. Currently, I am designing and printing connectors so I can make frames out of 6mm wooden dowels, and they're coming out perfect! I even made a dowel connector that connects to my Arduino mount instead of screws. Effectively, I am hoping to have a fully modular array of connectors and mounts to mount all sorts of Arduino modules.
keep up printing, you'll see, it gets faster and easier when you know what settings to tweak for what types of prints :)
what program do you use and is it free?
Nathan Green Tinker Cad is a free web based 3d printing design software
next you need to do a drop test see which one bounce more
I suspect there's a lot of variables in this. For instance, would one of them bounce better with higher infill, but not as good as the same with no infill?
That would be cool
3D Printing Professor he would print them all the same
Hadn't tried any of these type, cool! My favorite I've tried is Cheetah. It's perfect for Witch King of Angmar gauntlet parts that then get heat molded for a custom fit 😁
NICE JOB!!!
Nice, I tested 3 flexi/semi filaments on the robox, your right the slower the print the more reliable, I had trouble with ninjaflex, and really flexible material, wouldn't feed or print at all.
I'm using a generic TPU (kind of the first one in the video) and I'm able to print it at 40mm/s with 6mm of rectraction without any issues (with a TEVO tarantula Pro, bowden extruder). The main difference I changed is to reduce the extruder tension to almost 0, and raise up the extrusion multiplier to 1.4, and it's working fine. I wonder if someone else already tried it.
I can vouch for Fiberlogy 40D and 30D (softer than 40D) flexible filaments - I tried both to print some RC car tires and they came out pretty good. Using the OpenRC F1 as an example - I would recommend the 40D for the front spoiler bumper as the filament is a bit more rigid than the 30D but still flexes well to lessen damage caused by impacts and crashes. The 30D filament is good for tires but you need to be careful with the number of perimeters and your infill type - I found 2 -3 perimeter walls and concentric infill made for tires that acted very similar to real-world pneumatics - turning your feed rate down to 75-80% of what you would print PLA also helps a lot.
Ninja Flex is my fav for anything I need flexible on a quad. I have gotten some 63A to print on Ender3(Amazon Basics). I have upgraded the base model Ender3 as follows: Capricorn PTFE, Changed to a 26 tooth extruder gear and sharpened it with a small dremel sanding disc at very low speed I was really trying to get rid of some burring that didn't get cleaned off at the factory, and I also printed the extruder clip that puts more spring tension on the material going through the extruder gear. Here's my settings: nozzle size .36, flow to 105%, print in .16mm or smaller layer heights, only 40mm\s on print speed, and change your infill and inner wall speed to match. I also printed the material at the top of its temp range. A slow go compared to the 92A Ninja Flex at 85mm\s infill and inner wall at 100mm\s
I appreciate that Fiberology seems to have tried to describe their filament characteristics in the name: "40D" implies a particular Shore hardness.
I'm test all Tpu hardness 65,75,95 and 98 on my flashforge Dreamer had no problem and come out perfect
i was expecting to see how ninjaflex stands in this lineup, darn
Tysen P Chances are the generic TPU results is what you're looking for.
Hi Professor, fancy meeting you here. Love your work too, and I like how you are happy to suggest and credit other people, like makers muse and teaching tech. Keep up the good work, it's appreciated by many people like me who live far away from you in australia. Teachers without borders...
Abrasion resistance testing would give useful knowledge too!
First time commenter on your RUclips. Have you ever used Filkemp Filaments? I have been very impressed on drastically I no longer waste filament. They also have a great TPU!
very very interesting ! thx
0:51 HAHAHA the most nervous laugh I have ever seen
love the video thank you
Read the title in Mr. Regular's voice: "which flex is best flex?"
mistaecco my flex is best flex because I bought it from a STORE
does it come in BROWN!?
Peter Schmidt what about NATURAL (off-white yellow)???
which is best to damped sound
TUP is good for stubby holders. Especially if you put a bit of texture on the outside. Remember to put a hole in the bottom though or getting the can out is a nightmare.
Someone told me you could print Flexible prints, and I didn't believe it, but holy crap, I gotta get some of these filaments!
@Angus: I'm wondering ; what about the grippy-ness of those materials?
I've used some TPC-flex in the past and prints where flexible, but still quite slippery.
I printed some rubber feet for f.e. a 3d printer, but the machine still slides on the table too easily.
Which filament can be used best for this application?
Winand D I have some NinjaFlex, I printed feet for my printer. They hardly move at all. Maybe it also helps if you change your bed material (glass/tape)
Alright, i should try some Ninjaflex then! I print on a Buildtak surface (sometimes on Kapton), so it does not leave any tape residu.
When I finally find some time I'll send you some really impresive Polish filaments. As Fiberlogy flexes are nice and easy, I have some real monsters in my closet.
45ShA anyone? Or 60ShA with 600% extension? or maybe you need high friction coefficient and soft touch flex?
There's one company here in Poland that makes I think 7 flexes each with different applications and chemistry.
No facy colours and spools though. Purely technical high-end stuff.
Can we have an update on this? I'm really interested in printing gromits and shock absorbing parts do understanding how I tell how elastic a filament is going to be would be great.
I just got a titan on my printer looking forward to trying some flex :) tho i don't have a cooling fan
I'm very happy with NinjaFlex, very flexi an printable on a Wanhao I3 Plus! I printed test seals for industrialcase!
thanks for the info! Could you also test brands such as Hatchbox and Sainsmart please, thanks!
Need some of the Fiberlogy for making faux starburst
for flexible bed adhesion, I really like dried gluestick, print sticks, but comes off easy
I'm new to 3D printing and having a blast. This video made me wonder if anyone with a duel extruder has attempt to print with both flexible and regular PLA? For example. Skull with standard PLA and outer skin being printed with one of the flexibles? Maybe for like a Terminator battle damaged bust that kind of felt like real skin.
i'm sure the infill pattern/shape matters a lot on how squishy it is tho.
what about soft pla.
I know it's a simple idea but how about skateboard bushings with different flexible filaments and see which works best? (Just for those who don't know the bushings are the rubber bits in the trucks that give the leaning resistance)
I'd recommend doing an update on this and run prints without the infill. The structured infill really limits the flex.
Angus your lightning is soo dim, you should invest in better lights, it will make your videos pop. Cheers m8 continue the good work.
Hi Angus, very nice video 🙂 What's your suggestion for a recycled TPU?
Good video :) A video on how to use flexible filaments with a bowden tube would be great.
If it's 1.75mm... you basically don't. You MIGHT be able to get away with vase mode printing but more than likely it'll kink in the tube and jam. If it's 3mm filament then just print crazy slow, like 10mm/s and it might work.
Thanks for the swift reply.
Maker's Muse I have printed NinjaFlex with a bowden setup. That works fine.
May I know which filament is good for making Spring
Great video. Have you tried placing PLA prints in a carburetor cleaner vapour bath to make them flexible?
THANKS FOR THE DUROMETER CHART AND CORRESPONDING HARDNESS APPLICATION. YOUR VIDEOS ARE THE BEST. I HAVE A TEVO TORNADO GOLD AND LOVE YOUR VIDEOS.
I'll be checking. Ur other videos currently looking into flexible material so I can print certain bits for costumes
I'd like to see how well they work with a bowden extruder.
Throughout the entire video, every time you showed printing on the I3 mk2, the purple dangling plastic kept distracting me. :P
Thanks Angus, great info!
Interesting videos. A little question, with 10 different possible infill in Cura2 for example, have you ever played with the infill kind to see the effect on "squishiness" of the object for a same infill %? I wonder if there is an impact.
You should make a PLA comparison video. I guess you could call it a PLA-A-PALOOZA!
It is the octopi suction cups that make it hard to remove. :)
Thank you for your review. Do you have a new favorite for something similar to the MakeShaper TPU 85A?
Man, I wish flexible filament could be made stiffer while on the roll, but flexible like rubber after printing.
Thanks for the information. I don't suppose anyone's had a look at the flexible filament from Jaycar?
nice video
Can you do a video on finishing flexible parts? I think Plastidip could potentially work because it's flexible but not sure if it will finish the part
Printed Overture TPU on Anycubic Kobra. It was a Tinker CAD model for a handle that had to be easy on the hands and had to slip onto my tool end. The auto feed required pushing in the filament until it stops, then getting the extrusion started. The hole in the handle where the end of the tool was about 18mm square and went in about 60 mm into the handle shopping 50mm before the end of the handle. I was concerned about what might happen at the end of the hole, but the Kobra bridged across the end of the hole and went on to the end of the handle. I wonder if PLA would have done the same.
Do a vid on how to put the flexion on the prusa i3 mk2
Wandering Eclipse Or a video how yiu build the flexion onto the wanhao!! you showed a little work-in-progress in a room tour. there you said, that it needs modifications to fit the wanhao!
Show us!!
LETS GET STARTED
@Makers Muse, can you review M3D's Tough Ink? it's supposed to be a flexible filament that you can control the stiffness in the settings as well as it's supposed to have great bonding. I'd love to see what you think of it
Blueprint3d flexible filament is crazy flexi too. I'd suggest you give that a go also.
For anyone out there that will be using "generic" TPU, increase your top layers by 3 to 5 depending on how much you want to slow down your print speed. I've noticed that if I add 4 layers I don't need to slow down at all. Of course, your mileage may vary.
Octopus' Octopi and Octopodes are all acceptable ways to pluralise octopus so use whichever feels most comfortable, also great video.
Which one is the stretchiest?
I wonder if it's possible to print a belt with flexible filaments. Like a GT2 for example, or some other not so tiny teeth but something that could be used in a custom project. Not that we "should" start doing that since I think it's more cost efficient to just order it online, but would be a nice thing to try!
Can you make a full hollow ball???
What % of fill and pattern?
How nay shells, and thanks for a great video as always.
Is your hotend improved to work with softer flexible filament? Very usefull video!
Hi angus I love the video!! Hey I was wondering may I use your music in my videos? They"re just so amazing!!
Thanks man. Sorry, music is made for my channel only to keep it unique.
Hi there, thanks for your video👍 just wondering is the flexion extruder a must? I probably only need to print the rubber tires for once and do not need to do it again. Do I still need to buy the flexion extruder?
Question: If you have to print a unit that's 24" long by 2-1/2" wide by 3/4" high.... BUT your table is only 10 or 11" long -- How do you do it? And assuming you would split the model how would you connect the 2 or 3 pieces together and still be flexible?
ha, just got an add, and the last sentence was, "more flexible rewards"
I can't find any videos that specifically talk about TPU shore hardness
now this is an intro my friend hahah
The tougher flex-fills could be great in high durability applications.
Some of the difference in "head squishiness" could be air trapped in some but not others. 3:06, 5:03, 6:58, 9:31(trapped) vs 8:48 (not trapped).
Also, is the level of infill identical in all cases?
Hi Angus I have a question. Have you ever tried flexible filament with the Cetus. I have a Cetus and simply love it. I've used PLA and PETG and it works like a champ. I've never thought of using flexible material because the Cetus software doesn't have a lot of option for retraction and the like.
If I were to print a frisbee, what should I use? I want something solid but soft at the same time. I don’t want it to shatter when it lands, but I don’t want it to bend like crazy either.