@@meddlehedd1194 If you can find ReBar on the Rockwell chart it will be down there barely above butter! There'a absolutely no need to preheat to machine. Hardening by heat and water or oil dunk is useless too!
аФтор, всю свою хорошую работу испортил заточкой болгаркой, инструмент не калится заточенным, сгорит режующая кромка и с такой закалкой этой фрезой, только в заднице ковырятся и да, фреза из арматуры, точно только для задницы.
maybe case harden also?
I'd like to see it cut, since it was "mild" steel...at least would work on aluminum or softer
Nice tool great work bro👍
Nice work sir 👍
it might cut wood
Solo podría cortar metales no ferrosos como aluminio cobre y bronce porque ese acero no es tan bueno es bajo en carbono
What gearing & lathe can cut this type of helix???
This is total bullshit! Not even worth explaining why!
Wakodahatchee Chris
why? Because he didn't show it cut or because you don't think it can cut?
@@meddlehedd1194 If you can find ReBar on the Rockwell chart it will be down there barely above butter! There'a absolutely no need to preheat to machine. Hardening by heat and water or oil dunk is useless too!
@@cdrive5757 even the high strength alloy rebar?
@@meddlehedd1194 Not enough carbon in it to be used as Tool Steel.
Steel strength and steel hardness are not synonymous.
@@cdrive5757 Yeah I briefly searched the web for C content and hardness of high strength rebar but couldn't find anything, Hence my question above.
аФтор, всю свою хорошую работу испортил заточкой болгаркой, инструмент не калится заточенным, сгорит режующая кромка и с такой закалкой этой фрезой, только в заднице ковырятся и да, фреза из арматуры, точно только для задницы.