- Hello everyone.
You may have experienced that the weld bead turns gray when TIG welding a sanitary pipe in the 5G position.
Today I will introduce another welding method to prevent sanitary pipe weld beads from graying out.
Compared to "WALKING THE CUP techniques", the working speed may be slower.
However, it has several advantages, so it is a sufficiently applicable welding method.
And by using pulse setting, it is possible to make faster and more beautiful weld bead.
These welding techniques will be introduced later.
Thanks for watching and have a nice week.
#sanitary
#pipe
#TIG
#welding
#brilliant
#ideas
#interesting
#HAGOJIBI
#videos 
Наука
Спасибо! Полезное видео не только для новичков, но и для опытных сварщиков. 👍
Nice video.
You explained and showed it very well! 👍🏻💪🏻
During my welder's examination (which is already 15 years old), I also welded stainless steel pipes (diameter 50mm, wall thickness 2mm). However, the gray color was not included in the assessment, and we also did not need formation. The workpiece was clamped at 45 ° and we should start at the bottom (6 o'clock), then once towards 9 o'clock to 12 o'clock and then from 6 o'clock after 3 o'clock to 12 o'clock.
I thank your channel and thank you for making this good effort to deliver this science and useful information to students and followers. I also add that you translated your words into all languages, and this is very interesting, as I understand everything you are saying. Thank you, my teacher
Привет! Очень хорошие ролики по аргонодуговой сварке. Одним словом специалист своего дела. Желаю только развития канала!!!
매주 좋은 정보감사 합니다!
Gracias maestro por otra buena clase , un trabajo impecable , un saludo cordial y por supuesto un gran like desde Narón , Galicia ( España ) 🤓 😜
Gorgeous! That's some very fine knitting, Sir. Well done, as usual!
Splendide travaille,Grace à vous on en apprend tous les jours.
Encore merci
Sos un genio! Saludos desde Argentina
L'angle de la torche joue beaucoup sur la protection du gaz aussi. Je suis en train de souder une ligne d'échappement moto en 38mm et 42mm épaisseur 1.6 et même en tig pulsé si la torche et trop perpendiculaire au tube la protection se fais moins bien....du coup je vois que toi aussi tu orienté quand même bien ta torche vers l'arrière. Je l'ai fais aujourd'hui et ça fonctionne beaucoup mieux. Je suis à 160 ampères sans apport à 0,7 Hz parce que j'ai pas encore le coup de main pour les tubes, au moins je suis sur de pas trop chauffer. Le résultat est vraiment bien.
Merci pour tes vidéos 👍
Super cool.Thank you very much
That’s was awesome video
Exelente muy util tus tecnicas
Perfect for Sunday morning
좋은 영상 감사합니다 ~~
Здравствуйте, спасибо что делитесь опытом, у вас хороший канал, подписался и смотрю с удовольствием, 👍
깔끔하게 잘하시네요. 역시 👍🏻👍🏻👍🏻
Tenho feito muitos trabalhos como esse. Nunca usei essa técnica, faço sempre bocal colado. Vou testar essa técnica,pois, será muito útil locais de difícil acesso onde a tocha não cabe e dificulta a rolagem do bocal. Além de não queimar o acabamento a coloração interna fica sensacional. Seria legal , se você ,pudesse, mostrar essa solda numa boroscopia, para visualização, de coloração, fusão, fechamento da junta, olho, penetração. Obrigado pelos melhores vídeos de soldagem que você nos presenteia. É realmente um professor. Muito técnico.
Good student!
Nice sir
Great Weld. Meine Einstellung. 60 A, 6L Argon, 6mm Düsse , 1,6mm Red Nadel, 2T Modus mit 1 vor / 2 nach Gas. 2mm Nadel aus Düsse. Danke für deine Videos
Ist genau das was ich grad Brauche. Versorgungsleitungen für Kunststoff Material in nem Zuliefer Betrieb. Bleibe Dir Treu
Nice way indeed, thanks
Thank you so much.
大哥真的很棒 教學跟技術真的幫助我們很大～고마워요
Great 👌
딱 위생배관중인데 참고영상이네요 감사
very good job
Мастер ! Благодарю Вас!
great job
Como siempre.... Gracias
Muito boa a técnica. Simulando um cabeçote orbital. bom esse método em regiões difíceis. Já faço algo semelhante. Sempre com boas informações. 😃
You are best 🙏
굳입니다
Спасибо вам большое
Спасибо
Hola muy buen video, cual serian los parámetros con los cuales realizaste la soldadura,es para tener una idea de la configuración.gracias por tu tiempo.
Спасибо большое за Ваши видео. Очень сильно мативируете на развитие себя в области сварки. Я только начал этот путь.
На орбитальных головках примерно такая же технология только там ток не до нуля падает, а до 15 А если мне память не изменяет
Thanhks bạn thanhks. Quá đỉnh cao
형님 수고하셨습니다 😘
다른내용굼굼한대요 위빙할대 회색없시빽비드두나와는방법있읍요?...2t모드 4t모드큰차이있나요? 용접기 이기능없내요 😓
És um grande profissional !comecei no Inox a pouco tempo podes dar umas dicas de como ter noção que está a fundir por dentro?
Good 👍👍👍
Autogenious expert
thank you, it was very good and informative video. brother I have a question. can you recommend parameters for Pulse settings on the same tube on this video?
Mukemmelsin dostum ellerine sağlık seni seviyoruz.Yeni videolar bekliyoruz Turkiyeden Selamlar
Trop Bon soudeur 💪💪💪
good
펄스모드로 해도 괜찮을까요?
Nice:-)
ХОРОШО 👌.
보통근데. 봉은안대고나요??
저도 ns250fd 사용하고 샀습니다, 그냥 각파이프 용접할때 설정 좀 보여주세요, 부탁드립니다~~~
그간 현장에서 세니터리배관은 빽 나오면 무조건 결함이라 약전류로 비비기만 했었는데 이런 방법이 있었군요. 잘 배우고 갑니다.
спасибо очень полезное видео показывайте свои приспособления для сварки труб как массовый провод у вас закреплен тогда будет еще интересней спасибо
Сварка с поддувом всегда отличная. А вот сварки так же, но без поддува. Труба будет синяя.
구독자 1인입니다
질문이 있어요
업소용 스텐레스 대형 솥 내부를 알곤용접했을때 위생상 문제가 없는지 궁금합니다.
흠.... 동영상에 계속 위생 배관 얘기 나오는데요? 상식적으로 위생 배관 용어 자체에서 위생에 문제 없다는 건 유추 가능 하지요.
Great job as always master! Was there applied purging?
퍼징을 해서 파이프뒤에 용접비드가 나와 있네요 마지막영상부분을 잘 보세요
Great job, great job. I would like to ask you since you are a professional expert in this field and all your followers are witnessing this. So, I would like to ask you about a TIG welding machine that I found in the market, and it also has the feature of cold welding. You know that it is close to spot welding. I was hesitant to buy it because it works on welding thicknesses from 0.5 mm to 3 mm aluminum. And the rest of the metals from 2 mm up to 5 mm. And I would have liked more. Do you recommend it or is there a machine that recommends it.
There is a video about cold welding on my channel. The welding machine used in the video is a DC TIG welding machine optimized for thin sheet welding.
For more information about the welding machine, you can get a more accurate answer by contacting the manufacturer.
NSWEL's email
↓↓↓↓↓↓↓↓↓↓↓↓↓
korea@nswel.com
이 채널 때문에 전세계 용접기술이 상향평준화 되는 겁니까?
First of all, your video is really perfect, from the welding machine process to the welding experience, it is an expert-level sharing.
But laser welding machines will gradually replace traditional welding in the future. What do you think?
Not at all. Set up an automatic laser welding machine in a waterwall boiler welding replacement tubes into existing boilers, then get back to us
Could you make a video whit 2 mm thickness and filler metal?tanks
👍😍
bermanfaat
👍👍👍👍👍
Hàn rất tốt
圓管焊接點這麼密合
為何不用雷射焊效果會比較好
而且焊道也比較不會這麼大
배경음악이 좋네요. 용접강의 목소리는 더 좋네요.👍
👍👌🥇
top
learing to weld here - do people prefer to tig weld with a foot switch? I can't help but wonder if the switch in handpiece makes it harder to keep steady hand.
I weld sanitary stainless like in this video and build powder handling equipment and we all use a button on the hand piece, a foot pedal would only get in the way. Using 4T mode gets around having to keep pushing the button down. I personally usually use 2T for 90% of cases and don’t really notice having to hold the button.
👍
Is it correct to make exhaust welding with this welding method? Do you have a durability problem? with the wire method, the welding becomes gray in color and is subject to corrosion.please provide helpful information🙏🙏
퍼지는 꼭 해야 하나요? 안하면 어떻게 되나요?
토치 대갈통 ㅋㅋㅋㅋ 간만에 웃었습니다 형님..ㅋㅋ
크레이터 무 상태로 점용접해도 될까요?
물론 가능합니다. 하지만 직진도나 핀홀 확인 하면서 용접하려면 크레이터 있는것이 조금더 편할겁니다.
いつも興味深く拝見させて頂いてます。日本語訳を入れて頂ければもっと理解できるのですが…
🤩
6파이 0.16티 용접도 보고 싶네요.저는 일상적으로 하는거라 남이 하는것도 보고 싶네요.
E aí, beleza ? Você tem algum trabalho seu postado ? Gostaria de conhecer
0.16티면 엄청 얇은거 아닌가요? 전 다 녹아서 구멍 나던데ㅜ
혹시 다른 미국에서 유튜브로 세차하는거 하시는 분인가요?
몇일전 써니타리 작업을 했는데 1.5t였습니다. 근데 빽 내지말고 하라는데 ... 너무 어렵더라구요 ㅠㅠ 위빙도 하지말라그러고 훌치기로 빽내지말고 하라는데 전 도저히 안되겠더라구요..ㅠㅠ
저희 회사에서 사용하는 방법은
펄스용접입니다.
베이스 60A, 백그라운드는30A
레이팅은 좀 빠르게 하는게 유리합니다.
따발총 쏘듣이 다다다다요. ㅎ
마지막 끝처리는 다운슬로프2초정도
걸어서 돼지꼬리처럼 나오게 하구요.
이렇게 하면 빽도 안나고 용접속도도
잘나와 자주이용하는 방법입니다.
Merci beaucoup pour la vidéo , dis moi tu as changé de micro? on dirait que tu as une voix différente :) pourras tu faire une prochaine vidéo avec une épaisseur un peu plus grosse 2mm et métal d'apport? merci :p
Esse é um grande desafio mesmo. Solda sanitária com adição de material. Vamos esperar.
I'm a grey weld bead and I'm PROUD of it! All you shiny weld beaders have too much ego!
Lol tu sais je pensais comme toi avant et lorsque tu arrives à comprendre pourquoi c'est gris et que tu corriges en te rendant compte qu'en fait tu réglais mal ton poste ou même ta position de soudage ça fais plaisir quand ça brille un peu plus ☺️
Cordão cinza no inox é máquina alta amperagem! Inox sempre o mais baixo possível
펄스 쓰면 되는거 아닌가요?
아 뒷부분에 펄스 애기나오네여
I've welded clean room .065 sanitary tubing for 15 years, I've NEVER seen anyone do this... that should be 2 starts, and 2 pull outs, 6 o'clock-12 o'clock, twice. Done. Period. Starts and stops potentially let oxygen in and contaminants. They would laugh you off the job for doing this. High purity=no stops until bead in. Cleaning a restart on .065 is tricky and damn hard to keep clean. I wouldn't take anybody seriously after seeing them do this. Scotch Brite wheel on a drill.. No grey!
Inox 1,5mm mà mỏng.lạ vậy 🙄
Bocal colado
Технология очень похожа на сварку орбитальными головками
Этот аппарат варит весь цветной и черный металл?
Очень сомневаюсь что толщину трубы 1,5 мм , ток в 110 ампер не прожгет ее .. я бы варил на 55-60 амперах
용접 시작할때 숨 참은사람 있냐? ㅎㅎ
1,5мм я сварю без всякого импульса и отрыва, сплошным швом , попробуй сварить 0,2мм и покажи нам.
Never have i seen (in almost 30 years welding coded pipework) a procedure to stop/start a weld continuously. 65-70 amps, tight arc, no filler, then if it greys......
BRUSH IT WITH A WIRE BRUSH.
Problem solved.
Nie przejdzie do wycięcia jest kolor wewnątrz
反復機能無い溶接機なのか
WAYYYY too hot on amps, AWS certified in 6g position and running 38 amps and walking the cup will always leave proper and the most consistent penetration, your makeshift pulse method allows to many errors and inconsistent welds. But I'm sorry if I come across harsh i just believe everyone including myself has room for improvements!
GK paham
Тэбак
Don't be a gray weld
대갈통을 ㅋㅋㅋㅋㅋㅋㅋㅋㅋㅋ
Этот метод непрактичный.
Заебало слово "джимида"!!!