Why My TIG Welding Makes Gray Beads ??
![weld [HAGOJIBI]](http://yt3.ggpht.com/ytc/AIdro_lButtTy6bwshHHOdUuuc7ktsddm0YgRj2FhqoPUm3aQA=s48-c-k-c0x00ffffff-no-rj)
HTML-код
- Опубликовано: 10 июл 2021
- Hello everyone.
It is a process that everyone goes through at least once when learning tig welding.
I think you've probably asked the question, "Why is my TIG welding gray?"
I hope that today's video will be one of the processes to solve that question.
Thanks for watching and have a nice week.
#importance
#dating
#apps
#Shiny
#Rainbow
#argon
#Weld
#Beads 
Наука
Valuable information, one thing is reading from the book, and the other listening from a person with loads of practice.
感謝大師解說非常好的經驗!小弟受益良多!
氧化膜色澤 是溫度 與保護氣 配合控制出來的氧化膜顏色 ! 各類金屬加溫到發紅 約400度C 各類金屬大致上是這樣! 以不銹鋼來看 380度C ↑接觸氧氣 開始敏化變色 氧化膜色由 金> 粉紅> 紫> 藍> 灰> 一直到 母才加溫到紅以上400度C 瞬間離開保護氣 =黑灰色 也就是說 保護氣要是在母材完全退紅點降到380度c以下幾秒鐘後 才脫離保護氣 金屬原色才能展現 銀白色金屬原色 !
不鏽鋼! 顏色就是這樣在380~400度C之間接觸氧氣 造成氧化膜顏色變化! 有空用150A電流 制御調整點焊 鎢棒離母材越近 0.5秒按放 制御開關 瓷杯保護氣不離開 待母材發紅完全退卻2秒鐘後 看來應該是 銀白色!若母材發紅隨即脫離氬氣保護 氧化後就灰黑色! 以上我做過實驗 3MM不鏽鋼板料對接 全滲透L線 我加裝保護氣罩 約150MM長 電流50A 慢慢焊 焊1:1全滲透完 焊道是白銀色的不銹鋼原色 但是要是6MM厚板 相對的氣罩要加長!因為溫度降低時間較長! 至於 氬氣 調整 0-25L/min 那就要看 瓷杯口#4 ~#8 甚至以上 !瓷杯口越小氣流壓力越大 氣流調整越小 依照磁杯大小用耳朵聽氣體柔和聲音就好!沒一定值!不影響熔池為主!保護氣太大 在某些角度 條件會造成保護氣擾流 鎢棒不潔沾料 氣流由磁杯口通過阻力 產生倒漩流氧氣漩入造成氧化熔蝕! 在沒切設備下 TIG 小口徑慈杯 高流量氣體壓力 也可當做切割用!
不銹加溫至380度c 至400度c 當中接觸到氧氣氧化膜色澤 變化很多種顏色 控制這溫度範圍氧化膜可用於藝術展現 例如 氣機車不銹鋼藝術排氣管色澤!
為何課綱上鎢極徑 2.4mm 保護氣後流要設置大約7秒鐘左右 2.4鎢棒加溫到紅色 完全退至鎢棒原色 大約5秒 在給他兩秒保護時間 可保障鎢棒不受氧化效應 導致鎢棒熔蝕不銳利 影響電弧穩定性 這在手工 與自動化 焊接士非常重要的一環!那要是3.2mm 退紅點時間較長 保護氣後留時間可提升到9秒鐘!保護鎢棒本體不氧化 與焊道收尾!
當我們知道 不銹鋼在380度c以上會變為原色以外的氧化膜色澤 那就散熱治具 增加材料入熱與熱攜出程度
一般治具以成本 性質上 鉻銅較硬 在治具上加入循環水路那降溫更快 增加入熱程度更高 氣體保護降至380度C以下時間越短!可省保護氣體成本!
L線焊接 全線背護 面護 保護氣體 或是 氣密循環衡壓倉罩 也是保護金屬焊接完為金屬原色方法 但成本相對高!
以上是小弟20年前 在自動焊役接開發單位 曾經實驗過的結果 熔接工業一直在入熱 攜熱 溫度原理上 以及控制變型量 約束母材應力拉縮擴張與冷收縮上打轉 以上溫度原理交流希望在這工藝上對大家有一點幫助!感謝!
Коллега, ваши видео очень помогаю мне в работе, желаю вам всего хорошего)
I watch with translated subtitles and surprisingly I understand everything. Thanks for the help. I subbed
Excellent video.
You are an expert , thanks man.
Thanks for another nice video.
I'm gonna say this is what people does want to know and these little tips goes along way thanks alot great video
배움에 있어 경험치는 교본에 비할바가 못된다.
오늘도 한가지 배움에 감사드립니다.
이해가 너무 잘됬어요 ㅋㅎㅋㅎㅋㅎ 여태 궁금하던 사항들이었는데!!! 최고입니다
I learn many things while watching your videos, I know, I watch even if there are things, because everyone has a different solution and you can be sure that there is no good teacher like you in turkey, thank you very much
항상 좋은 영상 잘 보고있습니다~
선생님 고맙습니다
용접진행속도 입열량 다 문제가
없다고 생각했는데 제가 일반노즐에
과도한 가스양을 사용하고 있었군요
이제 회색비드는 그만 탈출하고 싶었는
데 정말 조언 감사드립니다
in the captions to english, iron should be steel instead :)
good information, ive been welding for 4 years and i learn something. you are a good teacher!
정말 배우기싶게 설명해주셧네요 감사합니다 !
Hey I love your videos they are very helpful and I was wondering if you could do some videos on tight gaps and big gaps 6g stainless pipe
매우 기본이되는 내용이면서 중요한 내용이네요 감사합니다 ~!
Доброго времени суток. Ещё не пробовал работать с TIG сваркой. Выглядит красиво. Хочется конечно попробовать.
Good job
Bardzo pomocny materiał 😀
Thank You from POLAND 👌
Muchas gracias por tus vídeos, eres un gran maestro 🙏
Awesome! Everything is true, if you let me to notice some moments plus, so, you can mention that if nozzle is too far because of cavitation can suck air and made gray weld bead, or if filler wire is not shilded also can make gray oxidation on weld bead, and same is with wolfram (tungsten), if is not clean can make dirty weld bead.
專業 鎢棒不淨沾料 氣流通過阻力 會產生漩流 帶入氧氣 氧化熔蝕!以往我持TIG直軟焊槍 應付高低間距20MM 深度200MM以上全滲透施工焊道 我都會把鎢棒 用乙炔 加溫 給鎢棒彎曲度 但角度不能超過杯口內徑 超過的話 保護氣通過鎢棒阻力 漩流會讓焊道熔蝕!這就跟沾料不淨的鎢棒是一樣道理!
One more thing, I was learning how to weld 2mm pipe cap pass for a while now and it kept coming gray ang gooey also the root pass kept melting and penetrating deeper than needed, I blamed my speed this whole time, no matter what settings I used it used to be all the same, today I found the problems solution- it was the angle of the electrode this whole time, the more perpendicular the electrode is to the surface of the pipe, the deeper it penetrates, so in order to compensate for that you need to decrease the angle... I was surprised how slowly can I weld without turning it gray. and the puddle looks exactly like in your videos... now all is left to improve my root pass because I used to get the same problem.
Коллега спасибо за объяснение!
비드에 굴곡이생기는이유가 용접봉 공급에불량이큰가요 ? 토치의 거리가 일정하지안아서 그런가요? ㅜ
Всё хорошо и доходчиво объяснил. Как всегда 👍
보니까 3M스피드글라스 G-02 용접면 쓰시는것 같은데 용접면에 대해 리뷰 한번해주세요 티그용접할때 아크색상이 파란색 인지 노란색인지 아님 회색인지 상세리뷰 부탁 드립니다
Thank you! Your videos are really helpful. A video regarding torch angle and tungsten stick out length would be really appreciated! 🙏
Good morning ... even your grey beads are nice though 🙂
Bonjour et super explication
главное-максимально возможная скорость сварки,а под свою скорость уже подбираешь ток, сопло и подачу аргона
Bery fun videos saludos desde colombia
아하~거의 노즐 사이즈랑같은 숫자의 유량을 사용하면 되군요. 감사합니다.
Excelente video, es d mucha ayuda, gracias por compartir tus conocimientos, fuerte abrazo desde Argentina
Ola donde se consigue esa makina
Big help putting this into practice tomorrow
목소리톤 얘기하시는거 은근 중독성이 쌔네여 ㅎ
좋은 영상 감사합니다👍👍
영상 항상 잘 보고 있습니다.
혹시 용접을 하는데 두께가 다른 모제 용접방법 알려주실수 잇으실까요..
수평으로 위에는 2티쯤 밑에는 7티쯤 되는 모제 입니다 ..
관련 내용과 비슷한 영상이 있습니다. 참고 하셔요~^^
Thank you.MASTER.
Super!
회색 비드는 꽃 피는 상태가 아니면 철브러쉬나 파워로 살짝 밀면 광택 납니다
Vos explications sont très claire, je vous comprend mieux que mon formateur, merci.
The heat input example using a cigarette is perfect 👌
Gracias por la explicación.
좋은 정보 감사합니다
Спасибо 🙏
Me gustaría ver, como cambia el color del cordón de soldadura mediante el largo del tusteno, saludos desde la Argentina
Thenk you my Sister im turkey.
top das galáxias parabéns ......
Frst cmnt bro please make s vdo on 6g tig and arc pls rquesr6 frm India
Good luck brother
Search for youtube abhimanyu welder
Felicitaciones 👍
非常詳細^~^
Good man
용접 교수님ㅋㅋㅋㅋㅋ
이미 회색으로된 것은 어떻게 처리해야 문제없게 되는 건가요? 긁어내기만해도 되나요?
👍👍👍
👍👏
Maestro 🙏
오늘도 좋은 정보 잘듣고 잘보고 갑니다...감사합니다
👍😍
Yes I am Argon welder 6 years Experience
Можно по подробней расказать тему расхода газа.
회색돼면 무슨문재 있나요?
현님 용접할대 빽비드나라구하는대 전류약하개하면 비드 안이쁜고.전류높개해면 비드가좀조와구회색됀미다...
Como siemrpe gracias. Saludos desde Ecuador
1:15 that is ok, i have an hour to spare.
👏👍👍👍
gracias
Hello, can you advise
👍👍
Спасибо! Супер!
티그비디오중 형님 영상이 세계 최고로 교육에 적합하다 봅니다
👍
👍👏👏
하고지비는 신이다!! he is god!!
I learned welding in korea, thanks to my previous company for employing me wayback 2008..
Qué tipo de gas es el que usa
Спасибо
ещё толщина присадки должна быть правильная, забыл чувак сказать
50 ㅡ25A. 용접시 넘 미끄러지고요 ..함. 올려주셍소
항상감사합니다
دائما تركز علي التلحيم .....ولكن استنشاق الغاز او المناطق المغلقة ..المفروض انه خطر ؟؟
始终专注于焊接......但吸入气体或封闭区域......它应该是危险的？？
감사합니다
얼마전 레이저 망막 수술받던 느낌이다..-.-
Master,,,,angkat aku jadi muridmu,,,pleace
오 ㅋㅋ내친구가 자기껀 왜 회색이냐고 물어봤을때 모른다 했는데 이제는 설명할수 있겠다 오 ㅋㅋ신기
تركب لاي مكنه ولا مكنه معينه اشتريها منين
좋은정보
왜 말을 마지막에 빠르게 하지 ㅋㅋㅋㅋㅋㅋㅋㅋㅋ
멋지게 하는건가요
대단한분 컥!
I'm just happy if I get a welding bead from my Tig efforts that is even and if it turns out dark grey or black ....so what, it still holds......colour is not an indication of weld strength or depth of penetration.......as you can tell, I'm not a welder per se, and just weld because I need to attach something to something else very firmly...... a touch with a grinder will make any weld pristine and a lick of paint makes it perfect.
텅스텐잡고 한번만 영상찍어주세요!!!
高溫回火後冷卻的顏色
Grazie molto interessante.
Poi fare una traduzione in italiano plis.?
行了反正簡單來說你焊完一個不要馬上移開繼續焊到底就這麼簡單OK？
보라빛청색만들고 싶어요
非常感謝你翻譯成俄語的朋友，你有很好的視頻
Too much heat its not complicated . Your stick out is fine . If its stainless you're carbinizing it . The hardest part of welding stainless is keeping it stainless . Turn the amps down you can see you're running too hot 🔥
问候你，我的兄弟，翻译就像你一样
Нихрена не понятно ,но очень интересно.
와 진짜 담배비유 지렸다