Is there anywhere that your notes are posted? if not thats okay as this is a very old video. However it would certainly save me time and allow me to have the diagrams!
Thank you, Mam, for this informative lecture which helps me to understand this Cooling curve, TTT and many other stuffs. I would give 100 likes if it's possible. Take my gratitude and keep doing good works :)
It's clear why onset of transformation gets quicker with larger undercooling (increasing delta g) but why that transformation begin time increases after some time ? In short why do we see a maxima like thing in ttt diagram ?
Very nice! Thanks! How do we define where the pearlite, bainite structures form on the IT diagram? All I have on my diagrams is F+C. Are all pearlite, bainite zones the same on all IT diagrams, regardless of carbon content?
3 Years later and still the best video on youtube teaching this! thanks from Canada!
Is there anywhere that your notes are posted? if not thats okay as this is a very old video. However it would certainly save me time and allow me to have the diagrams!
If I ever make it on this course you'd be quite the only reason. Thank you so much.
best professor, best explanation ❤
You are the reason I get A+. Huge thanks!
Good Stuff. Very well explained and easy to understand from the way you teach. Thank you!
thank you from Saudi Arabia, you make me understand more clearly .
Thanks from Middle of Nowhere, Arkansas
You are a very awesome human being!! Just watching this prepared me for the exam!
Thanks! Glad it helped. Good luck on the test.
Great explanation. You point out the parts we can have some hard time to understand makes me feel comfortable with the topics.
This was incredibly-well taught! Thank you very much!
thanks from egypt! ur better than my lecturer
wow amazing command over materials science! thank you
Finally understood after watching several other videos, thank you!
Thanks a lot, this video gave me a better understanding of TTT diagrams. :)
awesome mam your explain so nice and understanding easily
Thanks from Saudi Arabia
So very helpful and well explained, gonna ace this test 😂 thank you so, much from Charlotte North Carolina
Thanks from Brazil...
It's nice that anyone outside of my students actually wants to watch these. So thank you.
@@tonyacoffey5568 if i quenched quickly to 25 degree celsius and then reheated to 700 for 24 hours is it tempered martensite or spherodite
A LIFE SAVER ! thank you
excellent stuff
You're the best!
Thank you, Mam, for this informative lecture which helps me to understand this Cooling curve, TTT and many other stuffs. I would give 100 likes if it's possible. Take my gratitude and keep doing good works :)
Nicely explained.
thanks from Saudi Arabia too
well taught thank you very much!!!
Thank you too much it's was useful
thank u soo much noway you targeted exactly what I needed!
Thank you so much I finally get it
Wow! Thank you so much! I finally got it
Thanks, that was helpful
shit be gettin deeper bruh
thankyou
excellent , can you give me the presentation . it is very useful for me
Thanks a lot
thanks very much
It's clear why onset of transformation gets quicker with larger undercooling (increasing delta g) but why that transformation begin time increases after some time ? In short why do we see a maxima like thing in ttt diagram ?
Very nice! Thanks! How do we define where the pearlite, bainite structures form on the IT diagram? All I have on my diagrams is F+C. Are all pearlite, bainite zones the same on all IT diagrams, regardless of carbon content?
if i quenched quickly to 25 degree celsius and then reheated to 700 for 24 hours is it tempered martensite or spherodite
@Tonya Coffey
@@13-ahmedmohamedhassan73 Sorry. You'll have to do your own homework! I am a professor too.
@@tonyacoffey5568 that was a question on my exam. i have taken my exam since the last two days