Hi Tyler Let, (1) When is the Super Aiir Meter used? Immediately Between the mixing of the Concrete and the placing of the Concrete in the Pour? (2) If the Air Bubbles are too high, does adding more time to the Mixing Process help to Dispel more Air out? (3) Could / Should the Mixing of Concrete be STOPPED & POURING Started immediately when we have achieved the Perfect Number on the Air Meter? (4) Does the Mixing & Pouring In Multiple Small Batches help to give better Control Over the Air Bubbles than in Large Batches?l
_Great explanation. Please help me understand, then, why we vibrate fresh conctete? Wouldn't that change the SAM-measured void size and spacing by consolidating many smaller bubbmes into fewer large ones, thus making the concrete less durable in freeze-thaw performance?_
How do you control the air bubbels, I understand you can test for it, but when it is too high or too low, how can it be adjusted ?? would like a video on that subject. Because knowing something is good is nice but what kind of action is taken when it is bad ??
Dr. Ley, How did the "old school" Air Meter work as compared to the "Super" Air Meter? NEXT QUESTION:: is it Preferable or even Possible to use the Super Air Meter on even "Dry Cast" Concrete? THANK YOU.
Hey Been doing QC work for a few years now and ive got a question. You say large vs small air bubbles are why the concrete in the pictures was different. You then pitch the idea of your SAM which seems to only test bubble spacing. If you where to introduce one large (say 1"" ) air bubble into the pot during the test, from what your saying, Then the one two punch of your SAM method would produce very little difference in test 1 and 2. Because the large air bubble would not be knocked out by the test, you would get a low SAM number. So seems to me the test does not tell you if you have large or small air bubbles, but focuses on bubble spacing. Thing is, lots of bubbles clumped together isnt good for freeze thaw cycles either.. Ive watched all the vids regarding your air meter and plan on watching them again soon to see if i missed something. But from what i can tell now, your meter only tells you if there are big bubbles closely packed together, indicated by a low SAM number.. when a more uniform small bubble distribution may dissolve entirely giving you a large sam number. If small sam number is good, and Large sam number is bad.. this doesnt compute with me..
Thanks Darth, Please watch the videos again. Air void systems have both large and small bubbles. When I say "large" then that means on average the bubbles are larger. When I say "small" then that means the bubbles are on average smaller in size. Larger bubble systems for a given volume of air will be on average spaced further apart. If your bubbles are small then they will be spaced closer together for a given air content. The SAM can measure this. This is why it correlates to both spacing factor and freeze thaw durability. It does a much better job than just air volume. I show this several times. You are right that if one only had a few large bubbles then they would not dissolve under the pressures and the SAM Numbers would be low. However, that doesn't happen to our modern admixtures.
Excellent video!! Love the "upgraded" thinking and test method regarding air quality in concrete matrix.
Hi Tyler Let,
(1) When is the Super Aiir Meter used? Immediately Between the mixing of the Concrete and the placing of the Concrete in the Pour?
(2) If the Air Bubbles are too high, does adding more time to the Mixing Process help to Dispel more Air out?
(3) Could / Should the Mixing of Concrete be STOPPED & POURING Started immediately when we have achieved the Perfect Number on the Air Meter?
(4) Does the Mixing & Pouring In Multiple Small Batches help to give better Control Over the Air Bubbles than in Large Batches?l
That’s pretty awesome…. Really great work👍🏻
Thanks Dr. Ley, always excited to watch your videos.
Thanks Ali!
Ali - YES! When I talk about spacing factor then that is what comes from ASTM C 457. So there is a very good correlation between the two.
_Great explanation. Please help me understand, then, why we vibrate fresh conctete? Wouldn't that change the SAM-measured void size and spacing by consolidating many smaller bubbmes into fewer large ones, thus making the concrete less durable in freeze-thaw performance?_
so how do you make corrections to get the sam number where you want it just to keep from dumping the load?
Waiting your answer on this Dr. Tyler
My question is, say you do the test and get a given sam number, can the placement and tooling of the concrete have an effect on that number?
How do you control the air bubbels, I understand you can test for it, but when it is too high or too low, how can it be adjusted ?? would like a video on that subject. Because knowing something is good is nice but what kind of action is taken when it is bad ??
Great Question!
Dr. Ley, How did the "old school" Air Meter work as compared to the "Super" Air Meter? NEXT QUESTION:: is it Preferable or even Possible to use the Super Air Meter on even "Dry Cast" Concrete? THANK YOU.
Good video
I liked the information !
Hey Been doing QC work for a few years now and ive got a question. You say large vs small air bubbles are why the concrete in the pictures was different. You then pitch the idea of your SAM which seems to only test bubble spacing. If you where to introduce one large (say 1"" ) air bubble into the pot during the test, from what your saying, Then the one two punch of your SAM method would produce very little difference in test 1 and 2. Because the large air bubble would not be knocked out by the test, you would get a low SAM number. So seems to me the test does not tell you if you have large or small air bubbles, but focuses on bubble spacing. Thing is, lots of bubbles clumped together isnt good for freeze thaw cycles either.. Ive watched all the vids regarding your air meter and plan on watching them again soon to see if i missed something. But from what i can tell now, your meter only tells you if there are big bubbles closely packed together, indicated by a low SAM number.. when a more uniform small bubble distribution may dissolve entirely giving you a large sam number. If small sam number is good, and Large sam number is bad.. this doesnt compute with me..
Thanks Darth,
Please watch the videos again.
Air void systems have both large and small bubbles. When I say "large" then that means on average the bubbles are larger. When I say "small" then that means the bubbles are on average smaller in size. Larger bubble systems for a given volume of air will be on average spaced further apart. If your bubbles are small then they will be spaced closer together for a given air content. The SAM can measure this. This is why it correlates to both spacing factor and freeze thaw durability. It does a much better job than just air volume. I show this several times.
You are right that if one only had a few large bubbles then they would not dissolve under the pressures and the SAM Numbers would be low. However, that doesn't happen to our modern admixtures.
@@TylerLey thanks for the explanation I do agree 100% current methods of measuring air in concrete leaves much to be desired.