I will have to try that.. but, the bladss are too thick and the cutting angle way too steep.. Be great with a blade about 0.060 thick and a flat grind from cutting edge to the top.
Hi, i wondered why you are first hardening the blades an then putting the edges on them. Wouldn't it make sense the opposite way, so the steel ist soft while grinding it? I would be very thankful of you could answer :)
Sometimes when you harden thin edges they crack...depending on the specific alloy he's using, that is likely the case. It's definitely easier to grind while soft, but it's often safer to grind after heat treat.
Uz sve alate koje si nam pokazao u clipu, mnogi su vjerovatno propustili najbitniji. Tvoje ruke. Svi su alati bitni i olaksavaju posao, ali bez pravih ruku svi su alati bezvrijedni. Duboki naklon majstoree...
Hello!! Out of curiosity, what settings did you use to mark the stainless on your A40640? Thank you! I noticed 400mm/m and 100% power? I can't get mine to mark at those speeds for my life lol!
![Blox Fruits Dragon Rework Update [Full Stream]](http://i.ytimg.com/vi/EqDAp8udhm0/mqdefault.jpg)
Step 1: Get a Laser
Did you know there are other ways to draw a pattern on a piece of steel?
or just trace with a sharpie?
beautiful work
Beautifully made
Good to see ya.Very Nice Carving Blades
👍🏻🌟👍🏻
Nicely shaped handles. 🔪🎸
Hello AV beautiful knife's professionally made good job well done
Great work.
Nice blade man, just about to make some carving knives of my own soon
Buat ngiris bawang
I just made a caving knife about a week ago.
what steel are you using
Now all i need is a huge factory and I can make a carving knife 😅
Or a grinder and a drill.
thats cute!
I will have to try that.. but, the bladss are too thick and the cutting angle way too steep.. Be great with a blade about 0.060 thick and a flat grind from cutting edge to the top.
Hi, i wondered why you are first hardening the blades an then putting the edges on them.
Wouldn't it make sense the opposite way, so the steel ist soft while grinding it?
I would be very thankful of you could answer :)
Sometimes when you harden thin edges they crack...depending on the specific alloy he's using, that is likely the case. It's definitely easier to grind while soft, but it's often safer to grind after heat treat.
Beautiful work.
At what angle is the sharpening of incisors?
Bedog
Đây có phải là dụng cụ làm vườn ghép cành cây không vậy ông? Tôi cũng thích nó.
Uz sve alate koje si nam pokazao u clipu, mnogi su vjerovatno propustili najbitniji. Tvoje ruke. Svi su alati bitni i olaksavaju posao, ali bez pravih ruku svi su alati bezvrijedni. Duboki naklon majstoree...
Beautiful words. Greetings from Poland. :)
What's your belt grinder?
Nice👍🔪!!
Hello!! Out of curiosity, what settings did you use to mark the stainless on your A40640? Thank you! I noticed 400mm/m and 100% power? I can't get mine to mark at those speeds for my life lol!
awesome
Nic
👍👍👍
👍
Zarti nije pametnije da nozeve brusis prije kaljenja i onda poslije kaljenja tek dobrusis i naostris
You've got to be kidding.
Absurd
No jodan... tiene una maquina bien "SOFISTICADA" para MARCAR el acero??? Yo creyendo que era para CORTAR 🤔
It's good to see Woodglut have new instructions to save my money and energy to build it.