Really like how, organized and meticulous you are. Safety is my number one priority when reloading. I am just now getting into 9mm reloading and your video has given me lots of confidence. I have been reloading for some time now, but has mainly been .38/.357, .44mag, .45 colt, .454 casull, 45-70, 460 & 500 S&W. Earlier today I ordered my molds 125 and 147 grains (LEE), dies, and starline brass. I too was wondering what mold you are using here as I own many MP brass molds so this gives me a reason to buy another. I will be shooting mine out of pistol caliber carbines, do you see any need to use +P brass? Also, how soft a lead are you casting with and do you worry about lead fowling even with the powder coating? Thank you in advance and for your dedication, it's greatly appreciated.
I have not done any P+ reloading . I use the MP 147 grain HP mold and cast HP's with half and half lead. Half Wheel weights and half pure lead. I get about a 7/8 hardness and just air cool. I did expansion videos on that. I never got leading with powder coated pure lead, but not going super fast either. They just did not fly straight for very long.
I an set on using the powder dispenser for small loads so it can't get double charged. Rifle there is no way to double charge most of my loads as it would overflow and be evident.
Thanks for the video. Was wondering which mold you used for the hollow points. Thanks again very informative video.
MP mold 147 grain .359 and a link is in the description.
Really like how, organized and meticulous you are. Safety is my number one priority when reloading. I am just now getting into 9mm reloading and your video has given me lots of confidence. I have been reloading for some time now, but has mainly been .38/.357, .44mag, .45 colt, .454 casull, 45-70, 460 & 500 S&W. Earlier today I ordered my molds 125 and 147 grains (LEE), dies, and starline brass. I too was wondering what mold you are using here as I own many MP brass molds so this gives me a reason to buy another. I will be shooting mine out of pistol caliber carbines, do you see any need to use +P brass? Also, how soft a lead are you casting with and do you worry about lead fowling even with the powder coating? Thank you in advance and for your dedication, it's greatly appreciated.
I have not done any P+ reloading . I use the MP 147 grain HP mold and cast HP's with half and half lead. Half Wheel weights and half pure lead. I get about a 7/8 hardness and just air cool. I did expansion videos on that. I never got leading with powder coated pure lead, but not going super fast either. They just did not fly straight for very long.
I an set on using the powder dispenser for small loads so it can't get double charged. Rifle there is no way to double charge most of my loads as it would overflow and be evident.