I can solve this issue and successfully rietveld( BiFeO3) XRD.Now I am working on (SrBi4Ti4O15) but facing different error when I am running like,no reflection found,there is an error in your input file , please tell me about that issues
Tell me the sample name. I hope you have not correctly put the atomic position. Download the cif and then import. Please mail me with the problems you are facing. Satya
Thank you sir, Am trying to refine a synthesized sodium silicate crystal xrd pattern against a cod 2106900 reference phase in fullprof and am get warning!! The fractional coordinate in almost the H exceeds 1.2!. Please is there a way i can remedy the warning as the refinement won't converge. While having a high chi^2 value of 13.9
If you want to dope a element at A site of B site of the BiFeO3, add the element in the atom information with the atomic positions of A site or B site depending upon the size of the atom/ Ion. foe example if i want to dope Lanthanum in BFO then i will use Bi atomic position of BFO for La. This procedure can be done if the lanthanum substitution dies not change the structure of BFO. You can use same R3c. But if the substitution of La changes structure, then you have to go for dual phase refinement. foe example, 15% of La doping drives the crystal symmetry to rhombohedral and Orthorhombic dual phase. So, I have attached 2 papers link for your reference. Please read, if you have any problem mail me. aip.scitation.org/doi/abs/10.1063/1.4916927?ver=pdfcov&journalCode=jap DOI:10.1088/2053-1591/abdd50. Enjoy. Regards Satya
Your question is hypothetical. Kindly give the name of the different phases in your samples so that I can suggest how to go for refinement. If your cif file is not available first go for indexing and find the lattice parameters. Then see all the possible space groups of the examined material reported in literature. This may be temperature dependence data or pressure dependent data. Check the PE loop. That will also check whether the space group is centrosymmetic or not. I am taking a example here. BaTiO3 is a prototype ferroelectric. It has R3m, P4mm, Amm2 and pm-3m space group possibilities. What ever you dope or how you prepare the sample it will be in this space group only. The best fit is your space group. I hope this is helpful. I can not write a lot here so sorry for that.
This a crucial case. Do the indexing. It will suggest a structure and lattice parameters. Then run the data in expo to find probable space group. Next do a polarization measurements to understand the space group is centro symmetrical or non centosymmtrical. Compare your structure with similar compounds. At end see the fitting with lowest chi2 of the each space group.
To make a IRF file you need to run a standard sample in the XRD diffractometer. You can take standard as LaB6. Run this sample in the machine and collect the information like two theta, fwhm, peak shape parameters. Check one of the example file in the FullProf and put your own data for LaB6 measurements. Enter the IRF file when you convert cif to PCR.
Dear Selvaraj, Kindly specify the exact compound and dopant that you are using. This is a general question. In the example video, the material was R3c space group BiFeO3 and its a perovskite. If I do a rare earth doping it will put chemical pressure at A site means Bi site. But substitution at Fe site do not introduce structure change. and the structure changes to R3c to dual phase R3c+Pnma. These are my papers for reference. 1. aip.scitation.org/doi/abs/10.1063/1.4916927 2. iopscience.iop.org/article/10.1088/2053-1591/abdd50/meta. Thus, please specify you sample and dopant so that I can suggest space group for you.
Hello, thanks for this tutorial. On the off chance you are still answering questions about this, is FullProf capable of multiphase quantitatvie analysis? The software I used for my school has been taken away and replaced with a software that consistently overfits data to the point that it cannot be used and I am trying to learn Fullprof to complete my paper. Before, I used RIR analysis to analyze a multiphase sample with cifs I saved to my computer, but Fullprof is not able to read the space groups from this. When I put in some space groups manually, I am told the spacegroups I insert do not exist (even though I am taking them directly from the CIF files and they are identical to what is on something like COD). Do you have any advisement on how to get past this issue?
Hello! Sir i have tried every possible video on the youtube to refine my data, and the least value of chi 2 is still not less than 8. Can you please do my refinement?
Thank you for the video. You have negative y-coordinate (atomic position) for Oxygen, you kept that value as it is throughout whole refinement. Why didn't you consider that one? Can we visualize the unit cell with your refined atomic position?
Will you do refinement for me as I have to submit a review in 2 days and am unable to correctly do this chi square reduces below 1 and rexp above 200. shall be thankful
The error in lattice parameter is only active when the refinement tick is active in the box. To see the error, first refine and then check in the output file or sum file.
@@physicsdoneright sir i need a help…i have created a separate data file that includes 2 theta min , max , intensity…but whenever we browse the xrd data file then its not showing in that folder…folder shows empty…i can not select any xrd data file..plz help me
@deepa mam u can also suggest something regarding this? sir i need a help…i have created a separate data file that includes 2 theta min , max , intensity…but whenever we browse the xrd data file then its not showing in that folder…folder shows empty…i can not select any xrd data file..plz help me
The thin film xrd backgrounds are very noisy. You can simulate a xrd graph to find the peak position. I will not recommend doing rietveld refinement for thin film xrds.
Hi, do you also know if it runs on MacOS? I have tried but everything works except loading background file and running the fullprof which generated that red colored data and fitted profile. Strange, but do you have any idea how to solve it?
You can start minimum with 10. The choice of this number basically depends on the convergence of the profile fit. You will know it after 2 to 3 cycles of run.
Average apparent size cannot be calculated (no size broadening)! Possible reasons: (1) The broadening of reflections is resolution limited (2) No size parameter has been refined (3) The resolution function is not properly given this issue generation on doing in fullprof. Another thing is that after following your steps, my chi-square does not decrease to near 1. It stays 68. I tried refinig atomic positon but On doingit doesn't proceed how to resolve this issue?? Another issue I am getting with doing gsas , I face a issue no reflection in the pwdr limit i do not get. I this it becomes after refining which leads to unrelaistic histogram scale factor and zero off set. what are ur views can i get ur contact??
Kindly check in PCR file what is the number below "job". If this is not zero make it zero. Alternative, you can name you data file and PCR file same name. Just check.
Tell me your Rp, Rwp, Rexp values. Tell me your how your took data means step size and data scan rate and range. Check in the SUM file that model is satisfactory or not.
Peaks are not fitted well. If you have completed all the refinements then i guess that your data collection may be creating problems. All XRD data are not eligible to make rietveld refinements. You need to take step size 0.01 min, slow scan rate 1 degree per min and range 10 to 90. You can still report with chi2 with value 5 but R paramo must be below 6 at least.
I have two quiries plz sir do reply 1) i dont have that third file which u were talking about . I have cif file and my xrd and copied the intensity and made a new dat. File. 1)I am getting cycle 1 and chi2 :558 . . How to proceed from here
Thanks for asking. To create data for IRF file you need to take a data for LaB6 in your diffractometer where you have taken your sample data under examination. Then from the xrd data of LaB6, find 2theta, Lorentzian shape and Gaussian shape parameter. Then keep the data in the format shown in rietveld example file. And finally run in the software
Thank you so much for this tutorial, I have a problem with my refinement of YBCO, The refinement won't converge and I'm having a chi^2 value of 0.145E+04
Hello sir, how are you telling that at 9.50 sec while you are running the fullprof software you mentioned that it doesn't converged or something...what does it mean and how you are telling that I mean under what basis?... Please reply
I keep doing the analysis as in your video and always getting "error on intensity file, check your instr parameter". Do you have any idea how to fix it? (My Ins = 0)
Please make sure you have prepared the intensity file in correct way. The intensity file must have intitial 2theta then space then step 2theta then space final 2theta. Then enter and paste all the intensity data. I hope your step size is not written properly. Note: First try to run the intensity file data in winploter, then run in full prof.
@@physicsdoneright it was a problem with .dat file indeed, thank you! Now I'm facing a problem with refinement - it is quite good (chi2=32), but one peak does not appear in it. (If I manually increase the scale it appears). I'll be grateful for any tips from you.
This is the same file that you saved under the name ‘data.data’. I observed that there was an error in saving it with the ‘.data’ extension instead of the correct ‘.dat’ extension.
Yes, I can understand your problem. This problem usually happens but I don't have a scientific suggestion for this. I copy the folder to some other place before running the fullprof.
For me after running, the blue colour is showing as straight line only instead of xrd graph. Also cycle 1 chi 2 : 00 is mentioned please identify the problem?
Hello Sir, Thanks for the video . I am trying to do reitveld refinement for my sample . But after doing all the steps when I start the refinement , I am getting an error like "error on intensity file, check your instrument parameter parameter". please kindly suggest me regading this.
This problem is due to step size or spacing issue. The input file format is wrong. Please check the steps as follows 1. Line 1: initial 2theta then space then step two theta then space final 2 theta. example: 20.00 0.02 79.88 (Note: Check your data. It may be up to 4 digit after decimal.) 2. Line 2: paste the intensity value Save in filename.dat
I want do size and strain analysis for CeO2, will you tell how to prepare IRF files, if possible please send model file. After refinement, using winplotr, I have generated IRF_HG. IRF_Hl, and IRF_Hpv. Using these files I have plotted in Origin, is this procedure is ok or not.
You can take any file format described in the fullprof examples files. To make a IRF file you need to run a standard sample like LAB6 in the same Diffractometer where you have take that XRD data of the sample and replace the lorentzian and gaussian components in the IRF file format and run the sample in full prof. Or you can do the BREADTH package which is much advanced for size strain (i have another video uploaded for that)
The displayed value of Rp and Rwp and chi2 at the end of refinements will decide the experiment data has converged to theory or not. Always check SUM file generated at output.
materialsproject.org/materials/mp-542920/. This is for LaFeO3 which is a pnma structure. You can you add one atom for Gd with same atomic position as La.
thank you for giving good information sir about me but we doped different materials like (NBT-BT-BFO ternary phase diagram) how to arrange the atom position, please explain me
Okay. I understood you question. NBT is R3c or Cm depending on Polling. BT is p4mm and BFO is R3c. So if you have ternary phase then you need a simultaneous 3 phase refinements. Yes that would interesting to see. Go to the phase in rietveld and add all 3 phases separately. Then refine.
What does it mean by converge? I did not get that. You repeated three times and finally told it is now converged. Can you please tell me how to know whether it is converged or not? Thank you for this insightful video.
It's written on the screen at the end of each run. When each run is conducted by changing a parameter and then parameter will reach its optimum value, it will show that convergence is reached.😊
@@physicsdoneright Thank your for your response. Still did not find the converge term in the screen. Sorry for that. Can you please send the screenshot by highlighting this? Thank you.
See the literature report value of thermal factors of the particular elements for the compound. And fix the value. Do not refine it. The thermal factors should be a positive value because it is the displacement in angstrom square.
You can start the refinements from 0.1 to the optimized refined value. You can also check previous refinements single crystal data of your samples. Note that B values not to be negative.
Yobs - Ycalc is a almost flat line (less than 200 points diff and major peak intensity is around 18000) yet Chi2 value is around 10, what can be the reason/reasons for this, Sir?
Thank you so much sir, it was very helpful but I still have some doubt, can you please make a video on how to refine the data if there will be shifting of hkl peaks to right and to left with doping.
Estimated values of Figures of Merit: goodness of fit (χ2), profile residual (Rp), weighted profile residual (Rwp), expected weighted profile residual (Re) and background corrected reliability (R) factors (cRp, cRwp, cRe) where to get these values?
Thank you very much for this tutorial. Can we convert PCR file to CIF file? I have seen an option for that, but am not fully aware of the process. And what if we have multiple phases in the pattern, can we get multiple phase information in PCR file while doing peak search and keeping the numbers less than 20, which is recommended to create PCR file via FullProf?
Thank you for your questions. 1. Certainly, you can convert PCR to CIF from the output option menu. But that file format is not in the standard format as per COD or other databases. If you want to create the CIF file please see the formats of databases. 2. Yes you can do multiple phase refinement and you can get the percentage of each phase. Kindly see my video for the rietveld part ii which is basic for dual phase or multiple phase. I always recommend to create PCR files from CIF files. If you will edit other PCR files to create your own sample PCR then some of the hidden parameters will have non zero value inside and the pattern will not converge to low rp or two values. I am happy to answer your question.
Thank you sir for the video. However, even after following each step it's not running for my case. Everytime it's showing, job interrupted and pattern 1 not found.
The TCH pseudo-Voigt profile function (Thompson, Cox and Hastings, J. Appl. Cryst. 20, 79 (1987)) is used to mimic the exact Voigt function and it includes the Finger‘s treatment of the axial divergence (L.W. Finger, J. Appl. Cryst. 31, 111 (1998)). I took it with an aim for crystallite size and strain calculations.
Hlo sir, hope you are Fine. Sir, in atomic scale parameters my software did not refine it. It shows the conv is not reached... I tried so many times but it only shows conv is not reached kindly guide me what should I do now... If I have to change the parameters or any other process then tell me how can I do. Thanks and regards
Hi, I had the same issue and tried increasing the number of refinement cycles (iterations) to 30 and then 50. Convergence usually reached before 50 cycles in each case. I hope this helps. Best.
Hello sir, can you explain how to do refinement for material whose CIF file is not available such as 6 elements how make the CIF file phase name and lattice parameter is know how to make the cif file plz help me how manual make Cif file
Dear Dr. I followed all the steps but the lowest chi2 value I could get is 6.8. And I don't know how to proceed. Could you please help me? My material is cubic BaTiO3.
You can refine the following parameters such as anisotropic thermal factors, use of IRF file, different background files, peak asymetry. I note that if your rp, rwp, rexp are still less than 10, you can still report higher chi2 values even 5 or 6. If your data quality is very high means the data has been taken in very slow scan and step size 0.01, you may also get higher chi2. Poor data often gives low chi2.
@@physicsdoneright Sir, I have a DAT file. So without using CIF file downloaded from COD, I directly browse my data file in the pattern section and I have entered the values of lattice parameter, B, X, Y, Z, Oct and angles in the refinement section. After saving this, I have tried to run fullprof. But it keeps showing some error..
@@lekshmi833 please make sure 1. U, V, W parameter 0.06, -0.05, 0.08 put its starting value, 2. Then make sure you have chosen the right peak profile and shape
In theory xrd profiles are not broadened but due to crystallite size, strain and dislocation or due to experimental part, peak shapes broaden. So we need a instumental file that accounts for the broadening not resulted from the sample it's self. It's optional in fullprof. If you want to calculate crystallite size or strain from full prof, you may need that file. I can not write more here. Please see literature
This method is a structural refinement process that means you need to have a reference model. If you don't know the phase try to find the space group from various structural determination software.
Thank you for the tutorial video.... It's very helpful for the seeker like us ... Also due to elaborative explanation regarding each parameters it is unique for the refinement procedure... Btw I have a question regarding IRF file ... How can I get the IRF file??? Is there any issue if I used the IRF file of LaB6, given in example file.... If possible can I get your email ID???
Hello, take a xrd data of LaB6 from the same diffractometer from which you have taken your samples data. It is a property of the instrument. You can't use the lab6 file available in the example file of the installed software.
Dear Sir, I m doing all the steps according to you…but it shows the singular matrix errror… i need urgent of this…can i send u cif file and raw data file?
Dear, do not refine all the parameters at same time. If refining a parameter gives you singular Matrix then keep it fixed with its CIF file value. people often get singular Matrix dialogue box in u,v,w and occupancy refinement. Keep them fixed.
Hello sir.. thank you for the tutorial.. I am following the refinement process 10-12 runs, but still my chi2 value is 333 and the graphs r not converging. Is there any process to resolve it?
IRF is called an instrumental resolution file. You need to create that file. You need to take xrd data of Si or LaB6 in the same diffractometer where you have taken the xrd data of the sample to be refined. Kindly check my 2 videos in the playlist, how to create IRF files.
I too had this problem. The problem was with my antivirus deleting some important files after scanning for the virus. If u have an antivirus, try refining once before scanning or add FullProf files to ignore list. Hope your issue will be resolved.
Hi Sir.. Please mention ur mail id. I didn't found that on ur profile. I need to learn this software... I am having issue while puting pcr file b4 refinement
Sir can u please help me in this regard..i tried watching this video but facing some problems to do it.. can u please provide email id to reach u... For my research it's urgent
Sir, even though the cycles for refinement is given 15, only 1 cycle is running for me. I have tried so many times. What might the problem. Could you please explain it.
My Chi2 improved tremendously, thank you for the tutorial.
Glad it helped!
Our Xpert is now Online. Grt
Thank you so much, sir, for this great tutorial.
I want just refining graph that you create ,so where's I can ?
Please ask your question with more precisely.
I can solve this issue and successfully rietveld( BiFeO3) XRD.Now I am working on (SrBi4Ti4O15) but facing different error when I am running like,no reflection found,there is an error in your input file , please tell me about that issues
Check the intensity file and make sure that you have put the correctly wrote space Group.
Sir, it was great tutorial. Thanks a lot
how i can get the XRD data file (observed data) for the FeSb2 powder sample .
Or, is the data export from the cif file considered observed data?
Your question is not clear. The observed data is xrd data collected from diffractometer and calculated value if from cif file.
@@satyanarayantripathy Thank you, that's what I want
Sir i am doing refinement of my sample but at doing refinement of atomic position its show conver. Not yet reached... Pls help
Tell me the sample name. I hope you have not correctly put the atomic position. Download the cif and then import. Please mail me with the problems you are facing. Satya
Sir , can you upload reitveld refinement of carbon and ferrite nanocomposites ?
Thank you sir, Am trying to refine a synthesized sodium silicate crystal xrd pattern against a cod 2106900 reference phase in fullprof and am get warning!! The fractional coordinate in almost the H exceeds 1.2!.
Please is there a way i can remedy the warning as the refinement won't converge. While having a high chi^2 value of 13.9
Kindly mail me your data with the exact chemical formula and how you synthesized the sample. I will run it and let you know.
@@physicsdoneright thank you sir, ii have sent you an email with the required files
How would you handle a doped sample? It's very common to dope BiFeO3 with a number of different things and their aren't free CIFs for everything.
If you want to dope a element at A site of B site of the BiFeO3, add the element in the atom information with the atomic positions of A site or B site depending upon the size of the atom/ Ion. foe example if i want to dope Lanthanum in BFO then i will use Bi atomic position of BFO for La. This procedure can be done if the lanthanum substitution dies not change the structure of BFO. You can use same R3c. But if the substitution of La changes structure, then you have to go for dual phase refinement. foe example, 15% of La doping drives the crystal symmetry to rhombohedral and Orthorhombic dual phase. So, I have attached 2 papers link for your reference. Please read, if you have any problem mail me.
aip.scitation.org/doi/abs/10.1063/1.4916927?ver=pdfcov&journalCode=jap
DOI:10.1088/2053-1591/abdd50.
Enjoy.
Regards
Satya
Hello sir, can you explain how to do refinement for material whose CIF file is not available such as 4 to 5 elements high entropy material
Your question is hypothetical. Kindly give the name of the different phases in your samples so that I can suggest how to go for refinement. If your cif file is not available first go for indexing and find the lattice parameters. Then see all the possible space groups of the examined material reported in literature. This may be temperature dependence data or pressure dependent data. Check the PE loop. That will also check whether the space group is centrosymmetic or not. I am taking a example here. BaTiO3 is a prototype ferroelectric. It has R3m, P4mm, Amm2 and pm-3m space group possibilities. What ever you dope or how you prepare the sample it will be in this space group only. The best fit is your space group. I hope this is helpful. I can not write a lot here so sorry for that.
How can we do refinement for the compound whose cif file is not available
This a crucial case. Do the indexing. It will suggest a structure and lattice parameters. Then run the data in expo to find probable space group. Next do a polarization measurements to understand the space group is centro symmetrical or non centosymmtrical. Compare your structure with similar compounds. At end see the fitting with lowest chi2 of the each space group.
@@physicsdoneright
Is this possible to use 2 cif file for 1 compound, by the combination of two
@@sushiljoshi9655 yes. That is basically done for dual phase refinement. You can have even 3 cif files. That's the beauty
Thanku sir for such a great information but i have some doubt.......How to make IRF file
To make a IRF file you need to run a standard sample in the XRD diffractometer. You can take standard as LaB6. Run this sample in the machine and collect the information like two theta, fwhm, peak shape parameters. Check one of the example file in the FullProf and put your own data for LaB6 measurements. Enter the IRF file when you convert cif to PCR.
If doping, how to find the exact sym and wyck positions of newly dopent material? Can we choose ramdamly or any other else?
Dear Selvaraj, Kindly specify the exact compound and dopant that you are using. This is a general question. In the example video, the material was R3c space group BiFeO3 and its a perovskite. If I do a rare earth doping it will put chemical pressure at A site means Bi site. But substitution at Fe site do not introduce structure change. and the structure changes to R3c to dual phase R3c+Pnma. These are my papers for reference.
1. aip.scitation.org/doi/abs/10.1063/1.4916927
2. iopscience.iop.org/article/10.1088/2053-1591/abdd50/meta.
Thus, please specify you sample and dopant so that I can suggest space group for you.
I have uploaded a video on effect of doping and how to select atomic position. You can check.
@@physicsdoneright thanks sir, mine is R-3 and R-3m
Hello, thanks for this tutorial. On the off chance you are still answering questions about this, is FullProf capable of multiphase quantitatvie analysis? The software I used for my school has been taken away and replaced with a software that consistently overfits data to the point that it cannot be used and I am trying to learn Fullprof to complete my paper. Before, I used RIR analysis to analyze a multiphase sample with cifs I saved to my computer, but Fullprof is not able to read the space groups from this. When I put in some space groups manually, I am told the spacegroups I insert do not exist (even though I am taking them directly from the CIF files and they are identical to what is on something like COD). Do you have any advisement on how to get past this issue?
How , can I download spectra of given sample after refinement
Dear Sir, why 2 theta peak position is not copied in CIF file?
Thank you sir, how I can create IRF file for my sample. My sample is MOF
does the atomic position of each atom changes significantly while doing the refinement?
All atoms will not change sign. It may be possible that few atomic position may change sign.
@@physicsdoneright sir actually the fractional coordinate values changed significantly, like : 0.5 changed to more than 0.6
Sir, if I choose Occupancies unrecoverable divergence reached how to solve this?
Fix it as per the multiplicity of the site. Check the multiplicity number in cif file
Thank you sir
Hello! Sir i have tried every possible video on the youtube to refine my data, and the least value of chi 2 is still not less than 8. Can you please do my refinement?
Thank you for the video. You have negative y-coordinate (atomic position) for Oxygen, you kept that value as it is throughout whole refinement. Why didn't you consider that one? Can we visualize the unit cell with your refined atomic position?
Could anyone tell me how can I get cif file for rare earth doped ferrites
www.crystallography.net/cod/
rruff.geo.arizona.edu/AMS/amcsd.php
materialsproject.org/
icsd.fiz-karlsruhe.de/authorization/demoAccount.xhtml;jsessionid=5C7DA6584A48E1C66BBE61F51153FBC2
Will you do refinement for me as I have to submit a review in 2 days and am unable to correctly do this chi square reduces below 1 and rexp above 200. shall be thankful
If i didn't get CIF file for particular composites means what can do ?
I need to estimate error in unit cell parameter, please help
The error in lattice parameter is only active when the refinement tick is active in the box. To see the error, first refine and then check in the output file or sum file.
@@physicsdoneright sir i need a help…i have created a separate data file that includes 2 theta min , max , intensity…but whenever we browse the xrd data file then its not showing in that folder…folder shows empty…i can not select any xrd data file..plz help me
@deepa mam u can also suggest something regarding this?
sir i need a help…i have created a separate data file that includes 2 theta min , max , intensity…but whenever we browse the xrd data file then its not showing in that folder…folder shows empty…i can not select any xrd data file..plz help me
Please make sure that it is in dat format
Thank you for the Informations... can we use Rietveld refinement analysis for thin film samples..?
The thin film xrd backgrounds are very noisy. You can simulate a xrd graph to find the peak position. I will not recommend doing rietveld refinement for thin film xrds.
Hi, do you also know if it runs on MacOS? I have tried but everything works except loading background file and running the fullprof which generated that red colored data and fitted profile. Strange, but do you have any idea how to solve it?
I have no idea with Mac OS run of fullprof.
i'm running it on MacOS via wine-crossover. it works just fine
and why you chose 15 for cycles of refinement ?
You can start minimum with 10. The choice of this number basically depends on the convergence of the profile fit. You will know it after 2 to 3 cycles of run.
Average apparent size cannot be calculated (no size broadening)!
Possible reasons: (1) The broadening of reflections is resolution limited
(2) No size parameter has been refined
(3) The resolution function is not properly given
this issue generation on doing in fullprof. Another thing is that after following your steps, my chi-square does not decrease to near 1. It stays 68. I tried refinig atomic positon but On doingit doesn't proceed
how to resolve this issue??
Another issue I am getting with doing gsas , I face a issue no reflection in the pwdr limit i do not get. I this it becomes after refining which leads to unrelaistic histogram scale factor and zero off set.
what are ur views
can i get ur contact??
Sir I couldn't import data file in full proof suite, what to do?
Kindly check in PCR file what is the number below "job". If this is not zero make it zero. Alternative, you can name you data file and PCR file same name. Just check.
@thangamaalikad7790 are you able to do that? because I am also facing the same issue
When we click on RUN Full pruf after making PCR file we didn't get any FP file
I am doing your all step sir but my chi2 6.5 and please help sir how I can proceed for next?
Tell me your Rp, Rwp, Rexp values. Tell me your how your took data means step size and data scan rate and range. Check in the SUM file that model is satisfactory or not.
Rp45 Rexp 25 Rwp 50
Peaks are not fitted well. If you have completed all the refinements then i guess that your data collection may be creating problems. All XRD data are not eligible to make rietveld refinements. You need to take step size 0.01 min, slow scan rate 1 degree per min and range 10 to 90. You can still report with chi2 with value 5 but R paramo must be below 6 at least.
I have two quiries plz sir do reply
1) i dont have that third file which u were talking about . I have cif file and my xrd and copied the intensity and made a new dat. File.
1)I am getting cycle 1 and chi2 :558 . .
How to proceed from here
Increase number of cycles and start refining parameters in the list given in PPT. Anyways your question is very general. Kindly be specific.
Can you provide us the IRF file format or instruct how to create it
Thanks for asking. To create data for IRF file you need to take a data for LaB6 in your diffractometer where you have taken your sample data under examination. Then from the xrd data of LaB6, find 2theta, Lorentzian shape and Gaussian shape parameter. Then keep the data in the format shown in rietveld example file. And finally run in the software
Sir yah app nay 2theta ki values khud sa add kii hain ..?
Thank you so much for this tutorial, I have a problem with my refinement of YBCO, The refinement won't converge and I'm having a chi^2 value of 0.145E+04
Read some papers before running the package.. atleast the manual
Hello sir, how are you telling that at 9.50 sec while you are running the fullprof software you mentioned that it doesn't converged or something...what does it mean and how you are telling that I mean under what basis?... Please reply
Please read the output lines during each cycle run. It's written there
I keep doing the analysis as in your video and always getting "error on intensity file, check your instr parameter". Do you have any idea how to fix it? (My Ins = 0)
Please make sure you have prepared the intensity file in correct way. The intensity file must have intitial 2theta then space then step 2theta then space final 2theta. Then enter and paste all the intensity data. I hope your step size is not written properly. Note: First try to run the intensity file data in winploter, then run in full prof.
I also faced the same problem.Instead of uploading dat file we can upload .xrdml file by choosing PANalytical in the format.That helped for me
@@physicsdoneright it was a problem with .dat file indeed, thank you!
Now I'm facing a problem with refinement - it is quite good (chi2=32), but one peak does not appear in it. (If I manually increase the scale it appears). I'll be grateful for any tips from you.
This is a technical issue. Unless i know the structure, XRD data and space Group, i can not comment on your question.
@@physicsdoneright is it possible to reach you via other platform?
Hello sir, please let me know where from can I get the example BFO_DataFP since it is not available in website/example bundle.
This is the same file that you saved under the name ‘data.data’. I observed that there was an error in saving it with the ‘.data’ extension instead of the correct ‘.dat’ extension.
Sir, how to resolve invalid character in a numeric field
After this error all data in profile and atoms got swept
Yes, I can understand your problem. This problem usually happens but I don't have a scientific suggestion for this. I copy the folder to some other place before running the fullprof.
For me after running, the blue colour is showing as straight line only instead of xrd graph. Also cycle 1 chi 2 : 00 is mentioned please identify the problem?
Your question is not clear
Hello Sir,
Thanks for the video .
I am trying to do reitveld refinement for my sample . But after doing all the steps when I start the refinement , I am getting an error like "error on intensity file, check your instrument parameter parameter". please kindly suggest me regading this.
This problem is due to step size or spacing issue. The input file format is wrong.
Please check the steps as follows
1. Line 1: initial 2theta then space then step two theta then space final 2 theta.
example: 20.00 0.02 79.88 (Note: Check your data. It may be up to 4 digit after decimal.)
2. Line 2: paste the intensity value
Save in filename.dat
I want do size and strain analysis for CeO2, will you tell how to prepare IRF files, if possible please send model file. After refinement, using winplotr, I have generated IRF_HG. IRF_Hl, and IRF_Hpv. Using these files I have plotted in Origin, is this procedure is ok or not.
You can take any file format described in the fullprof examples files. To make a IRF file you need to run a standard sample like LAB6 in the same Diffractometer where you have take that XRD data of the sample and replace the lorentzian and gaussian components in the IRF file format and run the sample in full prof. Or you can do the BREADTH package which is much advanced for size strain (i have another video uploaded for that)
@@physicsdoneright Thanks for the information
How do you know convergence is not reached during run
The displayed value of Rp and Rwp and chi2 at the end of refinements will decide the experiment data has converged to theory or not. Always check SUM file generated at output.
@@physicsdoneright can you please explain in detail because I am new to refinement. Please.
Please call me over phone. My details available at info.
Sir how can we find CIF file for La0.75Gd0.25FeO3?
Pls help me sir
materialsproject.org/materials/mp-542920/. This is for LaFeO3 which is a pnma structure. You can you add one atom for Gd with same atomic position as La.
Sir, where you get the value of range?
You write in the notepad before copy intensity values
I did not understand your question. Please write in mail with detailed question.
thank you for giving good information sir about me
but we doped different materials like (NBT-BT-BFO ternary phase diagram)
how to arrange the atom position, please explain me
Okay. I understood you question. NBT is R3c or Cm depending on Polling. BT is p4mm and BFO is R3c. So if you have ternary phase then you need a simultaneous 3 phase refinements. Yes that would interesting to see. Go to the phase in rietveld and add all 3 phases separately. Then refine.
I have uploaded a video for Doped sample. You can check how to select atomic positions.
What does it mean by converge? I did not get that. You repeated three times and finally told it is now converged. Can you please tell me how to know whether it is converged or not? Thank you for this insightful video.
It's written on the screen at the end of each run. When each run is conducted by changing a parameter and then parameter will reach its optimum value, it will show that convergence is reached.😊
@@physicsdoneright Thank your for your response. Still did not find the converge term in the screen. Sorry for that. Can you please send the screenshot by highlighting this? Thank you.
Check time scale 7.30: it is showing normal end.
Check 9.49: it's showing convergence yet not reached.
@@physicsdoneright Ok, Thank you. I will check and let you know. Thank you very much.
cant fix the value of individual isotropic thermal parameter to positive value.alwayas one value become negetive .what to do.
See the literature report value of thermal factors of the particular elements for the compound. And fix the value. Do not refine it. The thermal factors should be a positive value because it is the displacement in angstrom square.
Please how we determine the values of B ?
You can start the refinements from 0.1 to the optimized refined value. You can also check previous refinements single crystal data of your samples. Note that B values not to be negative.
Yobs - Ycalc is a almost flat line (less than 200 points diff and major peak intensity is around 18000) yet Chi2 value is around 10, what can be the reason/reasons for this, Sir?
Kindly paste the output of sum file in the rietveld output
Thank you so much sir, it was very helpful but I still have some doubt, can you please make a video on how to refine the data if there will be shifting of hkl peaks to right and to left with doping.
Check my paper on Materials Science and Engineering B 294 (2023) 116511
sir cycles set ni ho rhy 15 krta hn dobra 1 ho jata ha \
Estimated values of Figures of Merit: goodness of fit (χ2), profile residual (Rp),
weighted profile residual (Rwp), expected weighted profile residual (Re) and
background corrected reliability (R) factors (cRp, cRwp, cRe) where to get these values?
Check the output file or SUM file
@@physicsdoneright okay sir, but which ones are the background corrected Reliability factors? cRp cRwp and cRe values
Thank you very much for this tutorial. Can we convert PCR file to CIF file? I have seen an option for that, but am not fully aware of the process. And what if we have multiple phases in the pattern, can we get multiple phase information in PCR file while doing peak search and keeping the numbers less than 20, which is recommended to create PCR file via FullProf?
Thank you for your questions. 1. Certainly, you can convert PCR to CIF from the output option menu. But that file format is not in the standard format as per COD or other databases. If you want to create the CIF file please see the formats of databases. 2. Yes you can do multiple phase refinement and you can get the percentage of each phase. Kindly see my video for the rietveld part ii which is basic for dual phase or multiple phase. I always recommend to create PCR files from CIF files. If you will edit other PCR files to create your own sample PCR then some of the hidden parameters will have non zero value inside and the pattern will not converge to low rp or two values. I am happy to answer your question.
Thank you sir for the video. However, even after following each step it's not running for my case. Everytime it's showing, job interrupted and pattern 1 not found.
Check the job is set 0
The job is set to 2, so should I make it 0? And also there are two patt# showning@@physicsdoneright
Sir, how to get an IRF FILE FROM REFINEMENT
Sir from where we can get IRF file?
Following
I am getting the error of reload .pcr file, if I click yes or No, nothing is coming afterwards. what could be the issue
I'm facing the same problem. Did u get any solution?
Can you explain why use tch axial input instead of pseudo voigt?
The TCH pseudo-Voigt profile function (Thompson, Cox and Hastings, J. Appl. Cryst. 20, 79 (1987)) is used to mimic the exact Voigt function and it includes the Finger‘s treatment of the axial divergence (L.W. Finger, J. Appl. Cryst. 31, 111 (1998)). I took it with an aim for crystallite size and strain calculations.
Hlo sir, hope you are Fine. Sir, in atomic scale parameters my software did not refine it. It shows the conv is not reached... I tried so many times but it only shows conv is not reached kindly guide me what should I do now... If I have to change the parameters or any other process then tell me how can I do. Thanks and regards
Hi,
I had the same issue and tried increasing the number of refinement cycles (iterations) to 30 and then 50. Convergence usually reached before 50 cycles in each case. I hope this helps.
Best.
Hello sir, can you explain how to do refinement for material whose CIF file is not available such as 6 elements how make the CIF file phase name and lattice parameter is know how to make the cif file plz help me how manual make Cif file
Tell me your sample chemical formula. Your question is not clear
Is it really necessary for the v value of FWHM parameters to be negative sir?
Yes
Dear Dr. I followed all the steps but the lowest chi2 value I could get is 6.8. And I don't know how to proceed. Could you please help me? My material is cubic BaTiO3.
You can refine the following parameters such as anisotropic thermal factors, use of IRF file, different background files, peak asymetry. I note that if your rp, rwp, rexp are still less than 10, you can still report higher chi2 values even 5 or 6. If your data quality is very high means the data has been taken in very slow scan and step size 0.01, you may also get higher chi2. Poor data often gives low chi2.
@@physicsdoneright Thank you Dr for the reply. I will try per your suggestions.
Greetings sir, hope u will b fine sir. Sir i am not abel to find any data neither in COD nor in ACD can u plz help my
My system is Yb2NiMnO6
Okay. The structure is a combination of 2 crystallographic phases. P21/n and R-3c. Try this dual phase.
Sir, after doing cif to pcr, in the pattern section I have tried to upload my data file. But it keeps showing the cif file I have uploaded earlier.
Please make your question clear.
@@physicsdoneright Sir, I have a DAT file. So without using CIF file downloaded from COD, I directly browse my data file in the pattern section and I have entered the values of lattice parameter, B, X, Y, Z, Oct and angles in the refinement section. After saving this, I have tried to run fullprof. But it keeps showing some error..
@@lekshmi833 please make sure 1. U, V, W parameter 0.06, -0.05, 0.08 put its starting value, 2. Then make sure you have chosen the right peak profile and shape
Sir what is the need of IRF files
In theory xrd profiles are not broadened but due to crystallite size, strain and dislocation or due to experimental part, peak shapes broaden. So we need a instumental file that accounts for the broadening not resulted from the sample it's self. It's optional in fullprof. If you want to calculate crystallite size or strain from full prof, you may need that file. I can not write more here. Please see literature
Is chi 2 value of 5.25 acceptable for research paper?
5.25 is allowed. if and only your data quality is extremely high with low Rp, Rwp, Rexp factors
Good morning sir..... If unrecoverable divergence occur what should we do??
Please make your questions certain.
hi, wht if we dont know the phase
This method is a structural refinement process that means you need to have a reference model. If you don't know the phase try to find the space group from various structural determination software.
ITS DIFFICULT BUT THANKS
@@physicsdoneright
Dear sir, could you please tell me the permissible value for Rp, Rwp and Rexp for reporting in a paper
www.cambridge.org/core/journals/powder-diffraction/article/r-factors-in-rietveld-analysis-how-good-is-good-enough/17439A1F889B689C495549A234D53682
Thank you for the tutorial video.... It's very helpful for the seeker like us ... Also due to elaborative explanation regarding each parameters it is unique for the refinement procedure...
Btw I have a question regarding IRF file ... How can I get the IRF file???
Is there any issue if I used the IRF file of LaB6, given in example file.... If possible can I get your email ID???
Hello, take a xrd data of LaB6 from the same diffractometer from which you have taken your samples data. It is a property of the instrument. You can't use the lab6 file available in the example file of the installed software.
Thanks, sir for the nice and valuable video, I need the Al2Mn2O7 compound atomic position for Rietveld refinement please provide me if possible.
or provide me cif file, I search COD but not able to find that.
_cell_length_a 8.181 _cell_length_b 8.181 _cell_length_c 8.181 _cell_angle_alpha 90 _cell_angle_beta 90 _cell_angle_gamma 90 _cell_volume 547.544 _exptl_crystal_density_diffrn 4.120 _symmetry_space_group_name_H-M 'F d 3 m' loop_
_atom_site_label
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
Mn 0.12500 0.12500 0.12500 0.89000
Al 0.12500 0.12500 0.12500 0.11000
Al 0.50000 0.50000 0.50000 1.00000
O 0.26550 0.26550 0.26550 1.00000
Try this one.
@@physicsdoneright Sir, compound belongs to monoclinic and space group is P2/m
sir how to make IRF file?
Sir, my pcr file on job column is not zero it is 2, whenever i load the pcr file it shows error what is the possible error
Put job 0
Now, it is saying check your intr parameters
Thanks sir its work
Check the spacing and initial, step and final 2theta in intensity data file
Sir what is singular matrix error while running
Dear Sir,
I m doing all the steps according to you…but it shows the singular matrix errror…
i need urgent of this…can i send u cif file and raw data file?
Dear, do not refine all the parameters at same time. If refining a parameter gives you singular Matrix then keep it fixed with its CIF file value. people often get singular Matrix dialogue box in u,v,w and occupancy refinement. Keep them fixed.
Sir When I am going to run after inserting the intensity data, It is showing too many points..
Can you please help Sir..
Mail me your data. Let me have a look. I think step size is very very small.
@@physicsdoneright Sir can you give your Email-id please.
Hello sir.. thank you for the tutorial.. I am following the refinement process 10-12 runs, but still my chi2 value is 333 and the graphs r not converging. Is there any process to resolve it?
Please send me you data with cif file. I will run and let you know. Mail me
Ok.. sure Sir
@@physicsdoneright the cif file of my sample is not available and i got the chi square 177 which taking the hypothetical data what can i do now
Tell me the sample chemical formula exactly.
@@physicsdoneright will u please send me ur mail id
Helo, Can you please share a video how to plot 3-D graphs of Reflection loss
That's easy with origin. You really need a video on that??
where do you obtain IRF file?
I have answered this many times. Please read other comments.
Hello Sir,
I have followed same steps as you have followed, I have encountered an error of too many position please help me out.
Please read the manual before running the package.
Can you do for me my sample is La Sr Mn O3
It's a easy structure. R3c or pnma may be. You can easily get the CIF file.
Good Morning Sir .How to download IRF File sir.
IRF is called an instrumental resolution file. You need to create that file. You need to take xrd data of Si or LaB6 in the same diffractometer where you have taken the xrd data of the sample to be refined. Kindly check my 2 videos in the playlist, how to create IRF files.
@@physicsdoneright thank you sir
After doing all the steps i am not able to run the program
I too had this problem. The problem was with my antivirus deleting some important files after scanning for the virus. If u have an antivirus, try refining once before scanning or add FullProf files to ignore list.
Hope your issue will be resolved.
i have biggest doubt in dat file making
i need tutorial for dat file making
Hahaha 😂
If job is not zero then??
Yes
Hi Sir.. Please mention ur mail id. I didn't found that on ur profile. I need to learn this software... I am having issue while puting pcr file b4 refinement
@@physicsdoneright Sir need to know one thing, in the intensity file, u have written 0.02 value, where does it come from?
It is the step size of 2theta
Hello sir I have mailed you regarding my problem please sir help me
Kutch Tunnel
Sir can u please help me in this regard..i tried watching this video but facing some problems to do it.. can u please provide email id to reach u... For my research it's urgent
Email id is given in the channel enquiry page.
Sir unable to find ur email id ..i tried...can plz send here for few minutes
@@physicsdoneright thank you Sir
sir whats your email
sir my elements are co zr fe o i am unable to find out CIF File for theses
Sir, even though the cycles for refinement is given 15, only 1 cycle is running for me. I have tried so many times. What might the problem. Could you please explain it.
Are you working with Bismuth Ferrite?
How to find IRF file?
I have answered this question many times in the comments.
how to download irf file?
How to do if CIF file not available
Mention the name of the compound
@@physicsdoneright Al4Cu9
how to get irf file
how to find irf file ?
Check my videos on how to make irf files
Sir my dat file is not appearing in the folder what should i do