NEVER going-back to freehand grinding after this!
HTML-код
- Опубликовано: 14 окт 2024
- Fredrik ends up this amazing series by starting the video with his heat treatment process, grinding the initial bevels using this amazing knife jig by Oliver Tobin, polishing the belts and finishing with style!
Hard Wax Oil: amzn.to/3sqdRa0
3M Peltor III ProTac Ear Defenders with Active Noise Cancellation: amzn.to/3POhqOT
Fredrik Spåre www.spareknive...
Knife-making classes in Sweden: www.spareknive...
Instagram: / fredrikspare
(===sponsor===) MULTITOOL PRODUCTS
Belt Grinders: (===sponsor===) MULTITOOL PRODUCTS (UK/EUROPE): www.multitoolp...
Evenheat Kilns: www.multitoolp...
(===sponsor===) CLARKE KNIVES
Buy a ready-made Damascus Billet: (===sponsor===) CLARKE KNIVES: www.clarkekniv...
Heat Treatment Services for Knife Makers: (===sponsor===) CLARKE KNIVES HEAT TREATMENT: www.vlakvarkfo...
Are you enjoying these knife making tips? Want us to make even more cooler videos? Support the UK Bladeshow and get a chance to win some lovely British-made knives: / ukbladeshow
Thanks again to all our Patreon Supporters and Promoters - YOU GUYS ARE THE BEST! / ukbladeshow
Super cool UK Bladeshow OFFICIAL merchandise shirts/mugs: ukbladeshow.cr...
#fulltimeknifemaker #knifegrinding #swedishknifemaker #kitchenknifesteel #knifesteelnerds #knifesteel #bestchefknife #chefknife #chefknifesteel
The simpleness of the serrations. Never thought of that.
What belts did you use after the 60 grit?
Tknx for this awesome video!
That was very interesting and contained much that other knifemakers have not explained .
Glad to hear you found it useful! Thanks for watching!
Hello, could you make a video explaining what a bimetal is and how they are used in knives. I am fairly certain I know what the meaning is as I am a metalworker, but there is uncertainty in the meaning for me.
Thanks😁
Ive seen a lot if old smiths use water on the anvil to pop scale. 🤝
Where can one buy the jig?
Thanks for sharing your process Fredrik and thanks for the creating this helpful content @UKBladeshow
Cheers bud! Nice to speak with you again today !
I like the overall process except for one small point. After normalising, Frederik then cold works the blade prior to heat treating. This may reduce the grain size in places to a point that some areas of the blade may not harden fully. I would be happier to see a second normalise at about 880C after all the cold working is completed.
Sparks are of no consequence. If the metal shows colour from getting hot when grinding then you could have a problem@alexander-iu8rr
Is that grinding jig available for purchase somewhere?
Hi Shaun, yes, it is available through Tobin Machines (Austria). You can also watch a video we did about grinding belt methods, including this jig, here: I tried this once and will NEVER freehand grind again!
ruclips.net/video/VEVmXViW34c/видео.html
- Vinz
So how are you avoiding cracks with all this cold forging?
If the steel is properly annealed, cold forging is not a problem
@@tobiashangler Ahhh! I somehow missed that these are annealed. Thanks!
If you set it on the anvil to cool, the anvil will act as a heat sink and it will not cool evenly.
👏👏👏🤜🤛
All jigs (including these) are limited to the style of knife you can do. And you cannot change the angle of the bevel your doing. The angle is at the mercy of the jig. Which is why freehand will always be superior
If you set it on the anvil to cool, the anvil will act as a heat sink and it will not cool evenly.