MOULD STEEL SELECTION IN INJECTION MOULD | IN HINDI
HTML-код
- Опубликовано: 4 окт 2024
- HI HERE AM WITH YET ANOTHER VIDEO ON MOULD STEEL SELECTION ,
AND BRIEF DETAILS ON STEEL STANDARDS.
ASSAB CHART:drive.google.c...
MOULD STEEL RECOMMEND
drive.google.c...
#VINDYCAD #INJECTIONMOULD #MOULDSTEEL
Can we do nitriding on stavax material
As per my experience.it is not needed..as Stavax (DIN 1.2083) ESR .
Its basically corrosive resistance and it has hardness range upto 56(+/-2 HRC ) at 1020°C
Or it will reach upto 57-58 HRC.
So nitriding or solid carborizing suitable for hardness ranges 36-38 HRc ( specially P20/ 718) tool steel or non cromo moly steel.
Thank you for asking question
@@VindyCADbruh... 😳😳 the level of Mettalurgy... Kudos. Vindy
@@VindyCAD😊
Your Video is more Knowledgeable and get more insight about metal
So please make such video
And we will appreciate your efforts.
1.Can You please tell us what is the Hardness of MS
2 Can we use MS for Core and cavity if not then Why
3 Why P20 is used for core and Cavity
Video is more informative 👌👌👌
Thank you.
1, hardness of ms 20-23 HRC
2.you can use for small quantity production.like 200 shots .
3. P20 has tendency to extract and release heat quickly.and has more corrosion resistance and good machinability and polish ability.
Thus P20 consider as tool steel preparedness is added advantage
@@VindyCAD thanku so much for your reply it add some value to my knowledge.
I'm hoping you get great success in youtube knowledge sharing channel
I'll definitely share your channel.
I'm interested and want one complet video on Complete Blow and Injection mould Design with some calculation.👍👍👍
Thank you sir what a great lecture 🙏
Great explanation....one more depth video on mold calculation with formulas...
Please make 1 video properly tool life & how many shots are guranty with different types of steel from tool manufacturing.
Super Explanation Sir
Thank you very much
Nice sir
WHAT A LESSON !!!!! AWESOME
Glad you liked it!
GOOD INFORMATION SIR
Good information...Thank you sir
Hi sir,
I really appreciate your efforts and sharing in depth knowledge on material selection and material properties. It will be really a great learning for me if you share some case study on core/cavity fracture failure in P20 material etc....
hi bro .. thank you for your words.. And i don't have any such case study things.documented..
But i recommend 6 million maximum shots..with good cooling..if you're not using p20 in good condition it will creep and become porous holes..beyond 6M.
Use P.20 Ni or 718 Chinese, PAC500
For good stiff and polish finish..
@@VindyCAD actually we have faced breakage issue in new mould even after 3000k shots...we have experienced 3 to 4 incidents till now...could you pls guide how to do case study on this?? So that it can be concluded with some report and standarization for future...no direct jumping to conclusions.....
@@VindyCAD Can we use alluminium if production quantity is upto 5 thousand Will it be good???
Hi, Which metal should be used for hydraulic press machine for plastic powder. Should have good abrasive resistance as well.
👍👍
Nice information 🙏
So nice of you
sir please make English video on the same material selection topic, it will be helpful globally 🙏🙏
Sure brother
Reale use full
GOOD INFORMATION SIR😍
Well explained..Thanks for valuable content..
So nice of you
Good
nice information. Kindly avoid background music
nice
Please suggest steel for crystal transperancy
sir kindly improve your audio quality please....thanks
Sir your lecture is the best but please fix the audio
Many of my friend subscribed your channel
Please do some video on press tool and design of jig and fixture
Thank you for considering.i can fix only after lockdown.
You may get relavent video soon on Press tool and jigs fixture.
Please respond how's audio quality now
Thanks
Please do videos in English 🙂. Thanks in advance
Pannala..thank you for responding.
👌👌
could you please tell why the stripper plate in injection preform molds from European manufacturer is of golden type metal...which metal is this?
It's TIN coated steel
Can you please explain about GB/T
High Polishing ke liye kon si elements ki main role hai
1.2316
Please suggest a material for PET Mould Inserts ( core cavity lip cavity)
Low production use En24 if high P20 HH also give good polisablity ( En24 not much you should make hard chrome )
I m confused b/w uddelholm nimax or stavax aka s136 bcs production is very high
P20 steel or S13 are named under which standards AISI, JIS or other?? and which standard is mostly use for naming steel and also alluminium???
DIN
EN31 k bare me bataye Nahi...
Hi, Just want to know that is 'S136' steel material good for injection molding mould for PP Material ?
If you are not using any fillers in PP material than you can use normal P20 .
If having fillers than S136 is recommended as it has good corrosive resistance. But need heat treatment.
Hello sir kya aap chennal join karte he to mould k problem solve karenge?
App problem batao..join sirf support keliye hai .ab me jyada active nahi hun..ap comment karke problem batavo
Hlo sir ye chat humko chahiye
Voice is not clear
Kannada..😉😉
Same here.
Great work, keep doing
Thank you brother!
Nice video 👍😊
Thanks for the visit
Please do in English bro
Pls improve voice clarity
Do in English bro.
Sure i try
Nice 👌