The molds fom the engine must be fully closed. That way you get good pressure wich is necesary to get sharp lines. Use a smaller ladl so you can poor more precisely. When pooring the white metal I use an electric toothbrush to agetate the mold and the molded white metal is spread evenly in the mold.
I found your channel a bit late, but I am amazed with your different approach to scale modeling. So cool. If I can help a bit, metal casting is a bit tricky, it's good you removed the top layer full of impurities. But for casting in forms, it's better to have some "valley" to pour the metal in, from which you have small channels to move the metal into the parts themselves. It's also good to pick in the "cold shield" on top of the puddle so you move only clean metal into the mold. Try to search for some YT videos and how to's. I think the block would be much better made from metal instead of resin. Give it a try once more. :) I'm cheering for you.
Thank you for all the advice. Metal casting is very difficult. I knew it wouldn't work, but I gave it a try. I'm thinking of trying it again someday. Thank you!
真空か遠心で鋳造しないと無理でしょうね。
メタルは何度失敗しても材料が無駄にならないのでいいですね
やっぱりメタル鋳造は遠心が必要ですね。。。
メタルはレジンと違って、何度でも使えるのが良いですよねｖ
プラモ製作って…奥が深いなぁ。尊敬しかない。
ダメっぽいのが分かっていながら、チャレンジ動画にしてみました。
一つのプラモでどれだけ楽しめるかも面白いところですｗ
良いものを見させていただきました🙏
鋳造のトライは素晴らしいです👍
いつかは必ず成功します🦾
ありがとうございました🙇♀️
ダメもとでチャレンジしてみましたが、やはりうまくいきませんでしたｗ
そのうちにまたチャレンジしてみようと思いますｖ
メタルを注型する時は型にヒートガンで熱を入れておくと流れやすいですよ。既にやっておられるようでしたら失礼。
温めた方がいいのは知ってましたが、ヒートガンという手がありましたね！ 持っていながら気づかなかったですｗ
Nice work making those parts. Thanks for sharing.
Thanks to you too! I'll try my best next time.
The molds fom the engine must be fully closed. That way you get good pressure wich is necesary to get sharp lines. Use a smaller ladl so you can poor more precisely. When pooring the white metal I use an electric toothbrush to agetate the mold and the molded white metal is spread evenly in the mold.
Thank you so much for all your advice! I will use it as a reference when casting again someday.
Thank you for sharing also your unsuccess.
Never tried White metal, process look very difficult to mastering.
White metal casting is very difficult. thank you as always!
I found your channel a bit late, but I am amazed with your different approach to scale modeling. So cool. If I can help a bit, metal casting is a bit tricky, it's good you removed the top layer full of impurities. But for casting in forms, it's better to have some "valley" to pour the metal in, from which you have small channels to move the metal into the parts themselves. It's also good to pick in the "cold shield" on top of the puddle so you move only clean metal into the mold. Try to search for some YT videos and how to's. I think the block would be much better made from metal instead of resin. Give it a try once more. :) I'm cheering for you.
Thank you for all the advice. Metal casting is very difficult. I knew it wouldn't work, but I gave it a try. I'm thinking of trying it again someday. Thank you!
スキルレベルと思考がマスタークラス！
自分も今そのキット作っています！
ありがとうございます！
このキットすごく楽しめますねｖ だけど完成までの道のりがとても長いですｗ
Good attempt 💪🏻👍🏻👍🏻
Thanks👍
このタイパの時代にホワイトメタルを溶かすだけに動画の半分を費やすところが大人のためのチャンネルですね
そうなんです。複製するところよりも溶かすところをメインにしたかったのかもしれません。
なるほど、微細な部品の鋳造は難しいのですね。
型の余熱や湯流れと界面張力の考慮など多くの要素が絡むという感じでしょうか。
そうですね～色々な要素が絡んで鋳造は難しいです。なんとも奥が深いです。。。
何か、川口の鋳物工場を連想してしまう私。
「キューポラのある街」古っ！（笑）
でも、よく考えてみると、エンジン部品は鋳物で出来ていたり
しますから、実はこの作業は理にかなっているのかなと
思います。
川口の鋳物工場の雰囲気、いいですね～ｖ
鋳造はうまくはいきませんでしたが、それっぽい雰囲気を制作の流れに取り入れられたかな～と思いますｗ
어떤 금속액체를 사용하셨는지 알고싶습니다!
주석이 주성분인 "화이트 메탈"이라는 메탈입니다. 저융점으로 부드럽기 때문에 취급하기 쉽습니다. 고마워!
@@Car_model_channel 인체에는 위험하지않을까요?
@@밤부우 화이트 메탈에는 납도 포함되어 있으므로 유해합니다. 사용할 때는 잘 조사하고 나서 사용하는 것이 좋습니다.
😱😱😱😱👍🏾perfection
Thanks!👍
How many enginees are u going to make?
😅
凄いな❗手間がモデルメーカー？
工業高校だったので実習の砂型鋳造したとき鋳口が少しずれて本体側に全然アルミ流れず砂崩したら鋳口部分のみ出て来てガッカリした記憶。
ありがとうございます！
砂型鋳造、やってみたいです！難しいでしょうね～
Try centrifuge casting that should sort all the problems
Thank you for your advice! I would like to try that method next time.
You need to dust the inside of the moulds with talcum powder before pouring the metal
Thanks for the advice!
お疲れ様です🍵
前段階の型取りシリコンゴムが耐熱用とは思って無くて、まさか今回ホワイトメタルの複製とは…！
市販のアプデパーツのST27やヒロ製のホワイトメタルパーツも、実際にはモールドが眠かったり、ダルかったり…と見かける事が多いですが、やはり難しいですよね〜。
途中で鍋に入れてたインゴット、パーツ端材が溶けて来た辺りのアク取り？が料理っぽくて良かった(？)です(((o(*ﾟ▽ﾟ*)o)))
お疲れ様です～
やはりメタルパーツ複製は難しいです。。。
ホワイトメタルのアク取り、面白いですｗ 少しずつ表面が奇麗になってきて病みつきになりますｖ
Половину ролика смотреть как плавится свинец, это конечно перебор.
Сцена получилась такой длинной, потому что то, как распутывался металл, было очень красиво.
ホワイトメタルでの複製って（笑）難しいんですね～🤭
うまく出来ないだろうな～と思いつつも、ダメもとでやってみましたｗ
First♥️♥️
Thanks!!!👍
何で上手くいかないんだよ
と、壁に投げつけムキーッ😂
エイッ！ヤーッ！って投げつけたくなる気持ちを抑えて、編集に没頭するのでした😅
良き鋳造のためには方案が肝要です。
ありがとうございます。
Well at least you have a great video for RUclips shorts.
Melting 🫠 is comforting.
I really like the way it melts.😅 Thanks👍
Your ladle needs a pour spout.
お玉には注ぎ口が必要です。
Otama ni wa sosogiguchi ga hitsuyōdesu.
Thank you for all the advice. I'll try the challenge again someday!