Dear Professor Hussin, your video is very helpful. May I ask some references that explain the Electrochemical Impedance Spectroscopy mechanism with this tool and and parameter values that need to be inputed in the software? Thank you very much ✨
Hi, please check my publications related to polymer electrolyte studies. I have used similar setup and all parameters are written in the article. All the best to you.
Thank you very much for this video, it is really helpful. When the Nyquist plot is a semi-circle, can the CPE with diffusion model be used to fit the curve, or else which model is preferable?
If the Nyquist plot shows a semicircle with a 45° line at the end (due to diffusion) of the plot, it is best to use CPE+Warburg impedance circuit for better data fitting
Thank you very much Professor Hussin for this useful video. I'd appreciate it if you explain how to save the fitting data in Gamry. + What are the components of "CPE with diffusion" circuit exactly? would it be possible to share with us the title of your publication in this regard? Many thanks
Thank you for your post. Well, to save the fitted data you can just save as the file after the perfect fitting has been done. It will be saved under .GData format
Professor Hussin, thanks for sharing your knowledge with this video, I'd appreciate it if you could tell why there is a relatively large value of Error with exponenstial of 18 for Rp in the video. Is this normal?
Hi, I would normally ignore the error values but will always refer to to the goodness of fit. If the goodness of fit is relatively low, then it means that the equivalent circuit used has a better fitting
Thanks for your video. By the way, where did you get this kind of cell for EIS test? I may purchase online. My sample is like sticky gel and I think I can also use similar ones. Another question is about the resistance of the cell itself. Had you deducted this value when you calculated the resistance of your sample?
That's a good question. Yeah, we have checked the resistance of the cell holder itself and because of the resistance value is too low the actual resistance of the sample is not differ much
In the case of corrosion, we look at Rp value. But since this video is more on finding conductivity of solid sample, the Rp or Rct is assumed as bulk resistance to be insert in conductivity formula.
Assalamualaikum Dr, i use the same setup as your for the solid polymer electrolyte usinf HZ7000 potentiostat. But for the nyquist plot my data is not a semicircle/straight it was scattered instead. May i know the possibility of this matter come from whether the sample of SPES itself or else. I use the same parameter as stated in the video. Thank you Dr
Well, scattered data points could from various reasons like poor interfacial contact between the electrode and the membrane, connection problem, sample is too thick or not homogeneous, disturbance from surrounding, wrong frequency range etc..perhaps you can check some of this reason
Dear Hussin, thanks for sharing your knowledge , I watched in the video , 9:40min , before user measured a sample thin film. is p-type silicon as a substrate and the film is Silicon carbide?. In addition is possible to send me the dimensions of the solid/film sample holder.
Hello Professor Hussin, I wanted to know whether you have conducted EIS with soil environment. If yes, please guide me through the procedure and difficulties associated.
Yes, i have tested soil sample as well but under two different conditions. 1. I run dried soil sample for conductivity measurement using EIS. For this purpose I use two electrode sandwich system. 2. I did corrosion monitoring of steel sample buried in soil. But it is not dried, it has at least 40% of water and for the reference electrode i have used silver wire, while counter electrode is graphite.
Assalamualaikum Dr Hazwan. Saya ingin bertanya, jika sampel saya adala film (starch+ graphene nanoplatelet) boleh tak saya gunakan kaedah rendaman (with an electrolyte and 3 electrodes) dalam melakukan ujian EIS
Wasalam, kalau nak lihat dielectric properties utk film tersebut lebih baik buat dalam keadaan solid state. Ini kerana bila kita rendam dalam electrolyte solution, polymer matrix drp starch serta ionic transport utk film tersebut sudah berbeza (dalam kes ini electrolyte yg memainkan peranan utk ionic transport, bukan film tersebut).
Thank you for uploading Dr. Hussin! Helped me a lot with my experiment!
@@anirudhsubramaniam3740 thanks!
Thank you very much for an amazing video! It was very useful and well explained.
Thanks
amazing video. it was reallllyy helpful
Thank you
Thank you very much for this video.
Thanks
Thanks for very informative video. May I know from where to get such type of cell? Thanks.
@@ashuntu2010 this is a fabricated cell..you can use a normal coin cell to run this experiment
Dear Professor Hussin, your video is very helpful. May I ask some references that explain the Electrochemical Impedance Spectroscopy mechanism with this tool and and parameter values that need to be inputed in the software?
Thank you very much ✨
Hi, please check my publications related to polymer electrolyte studies. I have used similar setup and all parameters are written in the article. All the best to you.
Thanks dear, what do you say about t at different temperature intervals, 20, 30 , 40 , 50.......80?
You need a stainless steel coin cell that can be put in an oven. From there you can study the thermodynamics
Thank you very much for this video, it is really helpful. When the Nyquist plot is a semi-circle, can the CPE with diffusion model be used to fit the curve, or else which model is preferable?
If the Nyquist plot shows a semicircle with a 45° line at the end (due to diffusion) of the plot, it is best to use CPE+Warburg impedance circuit for better data fitting
@@mohdhazwan6523 Thanks for your response. Can this model be applied if it's just the semi-circle without the line at a 45⁰ angle?
@@BerniceAbraham12 nope..better to fit it with normal Randles CPE circuit..without Warburg resistance
Thanks Sir, for taking out the time to reply.
Thank you very much Professor Hussin for this useful video.
I'd appreciate it if you explain how to save the fitting data in Gamry. + What are the components of "CPE with diffusion" circuit exactly? would it be possible to share with us the title of your publication in this regard?
Many thanks
Thank you for your post. Well, to save the fitted data you can just save as the file after the perfect fitting has been done. It will be saved under .GData format
Professor Hussin, thanks for sharing your knowledge with this video, I'd appreciate it if you could tell why there is a relatively large value of Error with exponenstial of 18 for Rp in the video. Is this normal?
Hi, I would normally ignore the error values but will always refer to to the goodness of fit. If the goodness of fit is relatively low, then it means that the equivalent circuit used has a better fitting
Hello Dr. Hussin just to confirm you are using a 2 probe setup with working and counter correct ?
@@XSD388 yes two electrode system..WE-(CE+RE)..meaning WE and CE short circuited with RE
Dear Hussin, thanks for the amazing video !! I have doped CeO2 powder, do I have to produce a film or a pellet to do the experiment??
In this case i would recommend you to make it into a pellet. Probably you can you FTIR pellet mould to do that
Dear Professor, thank you for sharing your knowledge. I wanted to know does this cell setup works for other type of potentiostat?
Yes, it works well with any potentiostat
Hello, can you tell me where you purchased the membrane sandwich holder...
It is a fabricated cell..you can find and vendor to fabricate it
@@mohdhazwan6523 please can you share the pics and dimensions with me, we are going to make it ..
Thanks for your video. By the way, where did you get this kind of cell for EIS test? I may purchase online. My sample is like sticky gel and I think I can also use similar ones. Another question is about the resistance of the cell itself. Had you deducted this value when you calculated the resistance of your sample?
That's a good question. Yeah, we have checked the resistance of the cell holder itself and because of the resistance value is too low the actual resistance of the sample is not differ much
OK. Many thanks. Did you purchase this cell? I may need a similar one to conduct my experiment.@@mohdhazwan6523
Hi please i want the setup for measuring impedence for membrane film where i can purchase in Japan
@@beshoynasr not sure where to buy in Japan but you can always search for stainless steel coin cell
@@mohdhazwan6523 thanks for responding I already use stalesteel one but there is no connection between stalesteel and nafion
Hello, can we say that Ru or Rp value is the corrosion resistance of material to solution ?
In the case of corrosion, we look at Rp value. But since this video is more on finding conductivity of solid sample, the Rp or Rct is assumed as bulk resistance to be insert in conductivity formula.
Assalamualaikum Dr, i use the same setup as your for the solid polymer electrolyte usinf HZ7000 potentiostat. But for the nyquist plot my data is not a semicircle/straight it was scattered instead. May i know the possibility of this matter come from whether the sample of SPES itself or else. I use the same parameter as stated in the video. Thank you Dr
Well, scattered data points could from various reasons like poor interfacial contact between the electrode and the membrane, connection problem, sample is too thick or not homogeneous, disturbance from surrounding, wrong frequency range etc..perhaps you can check some of this reason
@@mohdhazwan6523 Thank you Dr. really appreciate your explanation.
Dear Hussin, thanks for sharing your knowledge , I watched in the video , 9:40min , before user measured a sample thin film. is p-type silicon as a substrate and the film is Silicon carbide?. In addition is possible to send me the dimensions of the solid/film sample holder.
Yes we can run p-type or n-type semiconductor samples using EIS too. The dimension of the film was 1.5 cm x 1.5 cm
Hello Professor Hussin, I wanted to know whether you have conducted EIS with soil environment. If yes, please guide me through the procedure and difficulties associated.
Yes, i have tested soil sample as well but under two different conditions.
1. I run dried soil sample for conductivity measurement using EIS. For this purpose I use two electrode sandwich system.
2. I did corrosion monitoring of steel sample buried in soil. But it is not dried, it has at least 40% of water and for the reference electrode i have used silver wire, while counter electrode is graphite.
@@mohdhazwan6523 If you have taken the picture or created a video of the setup then can you please share it with me.
Assalamualaikum Dr Hazwan. Saya ingin bertanya, jika sampel saya adala film (starch+ graphene nanoplatelet) boleh tak saya gunakan kaedah rendaman (with an electrolyte and 3 electrodes) dalam melakukan ujian EIS
Wasalam, kalau nak lihat dielectric properties utk film tersebut lebih baik buat dalam keadaan solid state. Ini kerana bila kita rendam dalam electrolyte solution, polymer matrix drp starch serta ionic transport utk film tersebut sudah berbeza (dalam kes ini electrolyte yg memainkan peranan utk ionic transport, bukan film tersebut).
Hey, could you mind if you can send me the dimensions of the solid/film sample holder?
Thanks and looking forward hearing from you
This is a fabricated sample holder. I am afraid I didnt kept the drawing. But you also purchase a commercial coin cell for the same purpose.