@@HouseBrenn I’ll try to provide a straight answer! Each bike company does their own thing. Some remove carbon from areas that they feel is not necessary others who don’t. Usually with top tubes on modern carbon you will get flexing on the top part but not so much underneath and the sides. This is common and not dangerous. However if you press down like in this video or you hear a noise when you press. Then email us to assist with further advise no matter where you are. Thanks for asking the question ✅

@@darren7650 Hi there. The best is to contact CBR from the website and the office can tell you where we are regarding custom resprays. Thanks for getting in touch!

Thank you very much!

@@mreese8764 That’s not what he is saying..There are cases where some visible anomalies or traumas are showing inconsistent or inconclusive results depending where the issue is. There is no magic wand. What would you do as an inspector? It must be then be investigated by paint removal and then material removal if necessary. If it is not conclusive with the tests Rob mentioned then it cannot be ignored. Today we use scanning software which is more helpful but even so we would still remove material if we had any doubt. Hope that answers your question?

@@carbonbikerepair1 Yes. Than you!

I rode a 1” version of this for a while. Columbus is a reputable company. The 1” minimal is not as stiff as some forks but was perfectly ok

Nonsense. Aircraft testing equipment is nothing like a bicycle testing equipment. The word ‘aerospace’ is used a lot too. You don’t go to veterinary surgeon for your medical procedures..thanks you chiming in.

I heard this comment before and I understand where it is coming from but what you might not appreciate is what carbon bikes have become in order to stiffen thin walled frames which can measure 0.4mm in thickness. They are literally half the weight on average from 4 years ago. I would suggest to you then if you were in the business of repairing bikes by hand you might find that you can no longer claim to know if the repair is compromised because, as skilled as you might be, you have no reference. This system now guarantees these complex wall thicknesses remain. That alone, when you are repairing hundreds of bikes per month, is good enough for us. I see no other option to ensure the safety of the repair. Maybe in time there will be cheaper solutions forthcoming.

@@carbonbikerepair1 how are you identifying the laminate layup to ensure the stresses are distributed in line with the original? each layer needs to be replaced within 5 deg of the original to ensure as far as possible the integrity of the repair and not having a point of failure on the component, just replacing thickness isn't enough.

@@ChrisRawnsleyThank you for you comment. This is partially correct however layups vary across the areas of the bike as well as the brand process. There is no one way to successfully lay up a bike. The fracture location is therefore scanned with some impressive technology to identify the properties to replicate. Matrix ratios are also a big part of the makeup which is not often discussed yet critical in the character of the compliance as much as the architecture of the composite. Much of the process we are not permitted to show the public but replication is possible. As you suggest it is critical. Thank you

In this case the customer was given this as a gift from his father who passed away. Even so surprisingly still a lot cheaper than a retail value replacement frame at the time. This example is rare so it’s really just a show case of what is possible in the right hands. Thanks for your question!

Hello Tyler and friends. It’s impossible to be specific but I’m guessing your question is a universal one about the general robustness of the bb press-fit? Designers these days simply review past frame-sets and understand that there is a general rule when it comes to pressure applied + a bit more in case. Generally I would say the bikes in circulation will be up to the task of handling assembly and disassembly. When it comes to the individual doing it or the various types of oversize options available with scant information then anything is possible. I will say this as an experienced repairer though, often the damage is done before you hear that crack. It could be from a previous impact or stress applied to the bb. For example we have seen implosions of the bb just because no lubricants was applied to help slide in the bearing cups. To provide a universal answer: in general the carbon bb will out perform an alloy one when it comes to stiffness under load. Anything else and it is more vulnerable. Weight reduction, frame stiffness and mold shaping opportunities are some of the good reasons why we have so much carbon replacing alloy. Good or bad!

Yes some repairs are not economical but as you go up the cost scale that is where are kept very busy. Hopefully these example videos offer an insight to the secretive world of carbon repair. Thanks for your contribution

Good question. Tap testing is a waste of time because it is not definitive. You need to be sure either way otherwise there is no confidence in the result. The best way to test for ‘hidden’ issues at home is to compress with your thumbs across the tube. Listen for noise and feel for unusual give in the tube. If you have a duplicate of the part in question then reference that. Look for paint cracks but that too does not necessarily mean there is a fracture in the carbon wall. Best of all if you are unsure, get it to a reputable carbon inspector. Be careful..there are many waving ultrasound and aerospace talk. Avoid. Look for reviews and experience to assist.

Yes back to 100% otherwise it can’t be warrantied. Wall thickness and carbon fibre density the same. Have you got a problem with your bike?

We put in a bit to help to protect the rims. Also you never know if they might end up on a plane

Possibly because the aluminum can distort but generally the carbon fork will deal with an impact up to 7 times better as long as it’s not a sharp object impact but then it doesn’t matter both are going to land you in trouble

Hi there. Nope all should fine. In both cases, especially the heat, don’t leave it in that heat. If you ride it the air will keep it cool. Thanks for chiming in from Canada!

Sure as long as the clear coat is adhered otherwise take it back to bare carbon and key the surface

@@carbonbikerepair1 Great thanks for the reply. It is a 12 hour hardener was just afraid it might be an issue.

He doesn't know what he is talking about. They were never made in Malta or Far East. Also the Cielo was introduced in 2003/4 so not 30 years old.

Each table has an extraction system, I saw it mentioned in another video

ESPECIALLY to the eyes!

I came here as well to get an understanding of delaminating as well